Prediction of Ambient Pressure Conventional Superconductivity above 80K in Thermodynamically Stable Hydride Compounds

Antonio Sanna; Tiago F. T. Cerqueira; Yue-Wen Fang; Ion Errea; Alfred Ludwig; Miguel A. L. Marques

doi:10.1038/s41524-024-01214-9

← Back to search

Prediction of Ambient Pressure Conventional Superconductivity above 80K in Thermodynamically Stable Hydride Compounds

Antonio Sanna, Tiago F. T. Cerqueira, Yue-Wen Fang, Ion Errea, Alfred Ludwig, Miguel A. L. Marques

arXiv:2310.06804 · DOI 10.1038/s41524-024-01214-9 · 2023-10-10 · npj Computational Materials

T1experimental90 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The primary challenge in the field of high-temperature superconductivity in hydrides is to achieve a superconducting state at ambient pressure rather than the extreme pressures that have been required in experiments so far. Here, we propose a family of compounds, of composition Mg$_2$XH$_6$ with X$=$Rh, Ir, Pd, or Pt, that achieves this goal. These materials were identified by scrutinizing more than a million compounds using a machine-learning accelerated high-throughput workflow. They are thermodynamically stable, indicating that they are serious candidates for experimental synthesis. We predict that their superconducting transition temperatures are in the range of 45-80K, or even above 100K with appropriate electron doping of the Pt compound. These results indicate that, although very rare, high-temperature superconductivity in thermodynamically stable hydrides is achievable at room pressure.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Mg2RhH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	45	Pressure unresolved	unknown
Mg2IrH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	45	Pressure unresolved	unknown
Mg2PdH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	45	Pressure unresolved	unknown
Mg2PtH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	45	Pressure unresolved	unknown
Mg2PtH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	100	Pressure unresolved	unknown
SH3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	100 GPa	unknown
LaH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	250	170 GPa	unknown
CaH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	215	172 GPa	unknown
Al4H Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	54	Pressure unresolved	unknown
(Be4)2H Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	72	Pressure unresolved	unknown