Observation of high-temperature superconductivity in the high-pressure tetragonal phase of La2PrNi2O7-δ

Wang, Gang; Wang, Ningning; Wang, Yuxin; Shi, Lifen; Shen, Xiaoling; Hou, Jun; Ma, Hanming; Yang, Pengtao; Liu, Ziyi; Zhang, Hua; Dong, Xiaoli; Sun, Jianping; Wang, Bosen; Jiang, Kun; Hu, Jiangping; Uwatoko, Yoshiya; Cheng, Jinguang

Observation of high-temperature superconductivity in the high-pressure tetragonal phase of La2PrNi2O7-δ

Wang, Gang, Wang, Ningning, Wang, Yuxin, Shi, Lifen, Shen, Xiaoling, Hou, Jun, Ma, Hanming, Yang, Pengtao, Liu, Ziyi, Zhang, Hua, Dong, Xiaoli, Sun, Jianping, Wang, Bosen, Jiang, Kun, Hu, Jiangping, Uwatoko, Yoshiya, Cheng, Jinguang

arXiv:2311.08212 · 2023-11-16

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The recent discovery of high-temperature superconductivity in the Ruddlesden-Popper phase La3Ni2O7 under high pressure marks a significant breakthrough in the field of 3d transition-metal oxide superconductors. For an emerging novel class of high-Tc superconductors, it is crucial to find more analogous superconducting materials with a dedicated effort toward broadening the scope of nickelate superconductors. Here, we report on the observation of high-Tc superconductivity in the high-pressure tetragonal I4/mmm phase of La2PrNi2O7 above ~10 GPa, which is distinct from the reported orthorhombic Fmmm phase of La3Ni2O7 above 14 GPa. For La2PrNi2O7, the onset and the zero-resistance temperatures of superconductivity reach Tconset = 78.2 K and Tczero = 40 K at 15 GPa. This superconducting phase shares the samilar structural symmetry as many cuprate superconductors, providing a fresh platform to investigate underlying mechanisms of nickelate superconductors.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
La2PrNi2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	78.2	15 GPa	onset
La2PrNi2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	40	15 GPa	zero_resistance