Investigations of key issues on the reproducibility of high-Tc superconductivity emerging from compressed La3Ni2O7
Zhou, Yazhou, Guo, Jing, Cai, Shu, Sun, Hualei, Wang, Pengyu, Zhao, Jinyu, Han, Jinyu, Chen, Xintian, Chen, Yongjin, Wu, Qi, Ding, Yang, Xiang, Tao, Mao, Ho-kwang, Sun, Liling
arXiv:2311.12361 · 2025-02-05
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Recently, the signatures of superconductivity near 80 K have been discovered in the single crystal of La3Ni2O7 under pressure, which makes it a new candidate of the high-temperature superconductors dominated by 3d transition elements after the cuprate and iron-pnictide superconductors. However, there are several critical questions that have been perplexing the scientific community. These questions include (1) what factors contribute to the inconsistent reproducibility of the experimental results? (2) what is the fundamental nature of pressure-induced superconductivity: bulk or non-bulk (filamentary-like)? (3) where does the superconducting phase locate within the sample if it is filamentary-like? (4) is the oxygen content important for developing and stabilizing its superconductivity? In this study, we employ comprehensive high-pressure techniques to address these crucial issues. Through our modulated ac susceptibility measurements, we are the first to find that the superconductivity in this nickelate is filamentary-like. Our scanning transmission electron microscopy (STEM) investigations suggest that the filamentary-like superconductivity most likely emerges at the interface between the La3Ni2O7 and La4Ni3O10 phases. By tuning the oxygen content on the polycrystalline La3Ni2O7, we also find that the oxygen content plays vital role for developing and stabilizing its superconductivity. The upper and lower bounds of the oxygen content are 7.35 and 6.89, respectively. Our results provide not only new insights into understanding the puzzling issues in this material, but also significant information for achieving a better understanding on the superconductivity of this material.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| La3Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 80 | Pressure not reported | unknown |
Similar papers
Low volume fraction of high-Tc superconductivity in La3Ni2O7 at 80 K and ambient pressure
similarity 0.93Huo, Mengwu et al. · 2025 · arXiv:2501.15929
Source status unknown — claims are unverified
Unconventional Crystal Structure of the High-Pressure Superconductor La3Ni2O7
similarity 0.93P. Puphal et al.
Source status unknown — claims are unverified
Uncovering origins of heterogeneous superconductivity in LaNiO using quantum sensors
similarity 0.91Srinivas V. Mandyam et al. · 2025 · arXiv:2510.02429
Source status unknown — claims are unverified
Regulating oxygen content and superconductivity in LaNiO
similarity 0.91Peiyue Ma et al. · 2026 · arXiv:2605.04562
Source status unknown — claims are unverified
Single-crystal structural phase diagram of stoichiometric bilayer nickelate La3Ni2O7 under hydrostatic pressure
similarity 0.91Misaki Sasaki et al. · 2026 · arXiv:2607.27607
Source status unknown — claims are unverified
Identifying the structure of La3Ni2O7 in the pressurized superconducting state
similarity 0.91Hengyuan Zhang et al. · 2026 · arXiv:2511.15265
Source status unknown — claims are unverified