Antiferromagnetic Ground State, Charge Density Waves and Oxygen Vacancies Induced Metal-Insulator Transition in Pressurized La$_{3}$Ni$_{2}$O$_{7}$

Xin-Wei Yi; Ying Meng; Jia-Wen Li; Zheng-Wei Liao; Jing-Yang You; Bo Gu; Gang Su

doi:10.1103/PhysRevB.110.L140508

← Back to search

Antiferromagnetic Ground State, Charge Density Waves and Oxygen Vacancies Induced Metal-Insulator Transition in Pressurized La$_{3}$Ni$_{2}$O$_{7}$

Xin-Wei Yi, Ying Meng, Jia-Wen Li, Zheng-Wei Liao, Jing-Yang You, Bo Gu, Gang Su

arXiv:2403.11455 · DOI 10.1103/PhysRevB.110.L140508 · 2024-03-18 · Physical Review B

T1experimental

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

La$_{3}$Ni$_{2}$O$_{7}$ has garnered widespread interest recently due to its high-temperature superconductivity under pressure, accompanied by charge density wave (CDW) ordering and metal-insulator (MI) transitions in the phase diagram. Here, we reveal with comprehensive calculations that La$_{3}$Ni$_{2}$O$_{7}$ possesses an antiferromagnetic ground state under both low and high pressures, with the strong Fermi surface nesting contributed by the flat band that leads to phonon softening and electronic instabilities. Several stable CDW orders with oxygen octahedral distortions are identified, which can trigger the MI transitions. The estimated CDW transition temperature ($\approx$120 K) at ambient pressure agrees nicely with experimental results. In the presence of apical oxygen vacancies, we identify two different phases, say, half distortion and full distortion phases, respectively, and their competition can lead to a pressure-induced MI transition, in good agreement with experimental observations. In addition, we find that the electron-phonon coupling is too small to contribute to superconductivity. These results appear to indicate an unconventional superconducting pairing mechanism mediated by antiferromagnetic fluctuations. A phase diagram that is consistent with the experimental results is given. The present results not only explain the origins of experimentally observed CDW and MI transitions, but also provide insight for deeply understanding the properties like superconductivity, CDW and the role of oxygen vacancies in pressurized La$_{3}$Ni$_{2}$O$_{7}$.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
La3Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0	Pressure unresolved	unknown
La3Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0	10 GPa	unknown
La3Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	82	20 GPa	zero_resistance
La3Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	82	20 GPa	unknown
La3Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	75	30 GPa	unknown
La3Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	72	40 GPa	unknown
La3Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	50 GPa	unknown
La3Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.01	Pressure unresolved	unknown
La3Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0	10 GPa	unknown
La3Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0	20 GPa	unknown
La3Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0	30 GPa	unknown
La3Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0	40 GPa	unknown
La3Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0	50 GPa	unknown