Synthesis of $c$-axis textured CaKFe$_4$As$_4$ superconducting bulk via spark plasma texturing technique
Shigeyuki Ishida, Yoshihisa Kamiya, Yoshinori Tsuchiya, Pavan Kumar Naik Sugali, Yasunori Mawatari, Akira Iyo, Yoshiyuki Yoshida, Hiroshi Eisaki, Kenji Kawashima, Hiraku Ogino
arXiv:2403.19984 · DOI 10.1016/j.jallcom.2023.171093 · 2024-03-29
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Grain alignment is a key factor that determines the performance of a superconducting bulk. In this study, the spark plasma texturing (SPT) technique was used to fabricate a CaKFe$_4$As$_4$ superconducting bulk. X-ray diffraction and electron backscatter diffraction revealed that the $c$-axes of the CaKFe$_4$As$_4$ grains in the SPT bulk are aligned, demonstrating that the SPT technique is effective in achieving $c$-axis texture. In addition, chemical composition analysis showed that oxide impurities, which affect the grain boundary characteristics that determine the inter-grain critical current density ($J_c$), are randomly distributed in the SPT bulk. Magnetization measurements showed high $J_c$ values of the SPT bulk, reaching 127 kA cm$^{-2}$ and 26 kA cm$^{-2}$ at 4.2 K under a self-field and magnetic field of 5 T, respectively. These results suggest that the SPT technique is a promising approach for obtaining a high-performance superconducting bulk material for high-field applications.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| CaKFe4As4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Synthesis of CaKFeAs bulk samples with high critical current density using a spark plasma sintering technique
similarity 0.91Shigeyuki Ishida et al. · 2024 · arXiv:2403.19981
Source status unknown — claims are unverified
Ultra-high critical current densities, the vortex phase diagram and the effect of granularity of the stoichiometric high-Tc superconductor, CaKFeAs
similarity 0.84Shiv J. Singh et al. · 2018 · arXiv:1808.06072
Source status unknown — claims are unverified
Evolution of Critical Current Density in CaKFeAs with La-doping
similarity 0.83Yangsong Chen et al. · 2024 · arXiv:2412.03899
Source status unknown — claims are unverified
Realization of epitaxial thin films of the superconductor K-doped BaFe2As2
similarity 0.83Dongyi Qin et al.
Source status unknown — claims are unverified
Enhanced critical current properties in Ba0.6K0.4+xFe2As2 superconductor by over-doping of potassium
similarity 0.82Chunlei Wang et al. · 2011 · arXiv:1101.5427
Source status unknown — claims are unverified
Highly textured oxypnictide superconducting thin films on metal substrates
similarity 0.82Kazumasa Iida et al. · 2014 · arXiv:1410.8743
Source status unknown — claims are unverified