From weak to strong-coupling superconductivity tuned by substrate in TiN films

Yixin Liu; Yuchuan Liu; Zulei Xu; Aobo Yu; Xiaoni Wang; Wei Peng; Yu Wu; Gang Mu; Zhi-Rong Lin

doi:10.1088/1361-6668/ad7642

← Back to search

From weak to strong-coupling superconductivity tuned by substrate in TiN films

Yixin Liu, Yuchuan Liu, Zulei Xu, Aobo Yu, Xiaoni Wang, Wei Peng, Yu Wu, Gang Mu, Zhi-Rong Lin

arXiv:2404.16469 · DOI 10.1088/1361-6668/ad7642 · 2024-04-25 · Superconductor Science and Technology

T1experimental3 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The interplay between substrates and superconducting thin films has attracted increasing attention. Here, we report an in-depth investigation on superconducting properties of the epitaxial TiN thin films grown on three different substrates by dc reactive magnetron sputtering. The TiN films grown on (0001) sapphire exhibit (111) crystal orientation, while that grown on (100) Si and MgO substrates exhibit (100) orientation. Moreover, the samples grown on Si reveal a relatively lower level of disorder, accompanied by the higher critical transition temperature $T_c$ and smaller magnitude of upper critical field slope near $T_c$. Remarkably, we uncovered a rather high value of superconducting gap (with $Δ_0/k_BT_c$ = 3.05) in TiN film on Si indicating a very strong coupling superconductivity, in sharp contrast to the case using sapphires and MgO as the substrate which reveals a weak-coupling feature. The comprehensive analysis considering the scenarios of the three substrate shows that the grain size of the thin films may be an important factor influencing the superconductivity.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
TiN Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	5.14	Pressure not reported	midpoint
TiN Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
TiN Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
TiN Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
TiN Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
TiN Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
TiN Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
TiN Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
TiN Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown