Superconductivity in pressurized Re$_{0.10}$Mo$_{0.90}$B$_2$

S. Sinha; J. Lim; Z. Li; J. S. Kim; A. C. Hire; P. M. Dee; R. S. Kumar; D. Popov; R. J. Hemley; R. G. Hennig; P. J. Hirschfeld; G. R. Stewart; J. J. Hamlin

Superconductivity in pressurized Re$_{0.10}$Mo$_{0.90}$B$_2$

S. Sinha, J. Lim, Z. Li, J. S. Kim, A. C. Hire, P. M. Dee, R. S. Kumar, D. Popov, R. J. Hemley, R. G. Hennig, P. J. Hirschfeld, G. R. Stewart, J. J. Hamlin

arXiv:2408.17416 · 2024-08-30

T2theoretical

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The recent surprising discovery of superconductivity with critical temperature $T_c$ = 32 K in MoB$_2$ above 70 GPa has led to the search for related materials that may superconduct at similarly high $T_c$ values and lower pressures. We have studied the superconducting and structural properties of Re$_{0.10}$Mo$_{0.90}$B$_2$ to 170 GPa. A structural phase transition from R3m to P6/mmm commences at 48 GPa, with the first signatures of superconductivity appearing above 44 GPa. The critical temperature is observed to increase with pressure. A complete resistive transition is observed only above 150 GPa, where the highest onset $T_c$ of 30 K is also achieved. Upon releasing pressure, the high pressure superconducting phase is found to be metastable. During unloading, a complete resistive superconducting transition is observed all the way down to 20 GPa (with onset $T_c \sim 20$ K). Our results suggest that the P6/mmm structure is responsible for the observed superconductivity.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Re0.10Mo0.90B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	150 GPa	onset
Re0.10Mo0.90B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	20	20 GPa	onset
MoB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	32	70 GPa	unknown
MoB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	5	Pressure unresolved	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	203	155 GPa	unknown
LaH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	260	190 GPa	unknown
MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	39	Pressure unresolved	unknown
WB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	17	90 GPa	unknown
Nb0.1Mo0.9B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7	Pressure unresolved	unknown
Nb0.25Mo0.75B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7	Pressure unresolved	unknown
Nb0.5Mo0.5B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7	Pressure unresolved	unknown
Nb0.75Mo0.25B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7	Pressure unresolved	unknown