Magnetic field sorting of superconducting graphite particles with T$_c$$>$400K

Manuel Núñez-Regueiro; Thibaut Devillers; Eric Beaugnon; Armand de Marles; Thierry Crozes; Sébastien Pairis; Christopher Swale; Holger Klein; Olivier Leynaud; Abdelali Hadj-Azzem; Frédéric Gay; Didier Dufeu

Magnetic field sorting of superconducting graphite particles with T$_c$$>$400K

Manuel Núñez-Regueiro, Thibaut Devillers, Eric Beaugnon, Armand de Marles, Thierry Crozes, Sébastien Pairis, Christopher Swale, Holger Klein, Olivier Leynaud, Abdelali Hadj-Azzem, Frédéric Gay, Didier Dufeu

arXiv:2410.18020 · 2024-10-23

T2theoretical5 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

It has been claimed that graphite hosts superconductivity at room temperature, although all efforts to isolate it have been vain. Here we report a separation method that uses magnetic field gradients to sort the superconducting from normal grains out of industrial graphite powders. We have obtained a concentrate of above room temperature superconducting particles. Electrical resistance measurements on agglomerates of sorted grains of three types of graphite show transition temperatures up to T$_{c{_{onset}}} \sim$ 700K with zero resistance up to $\sim$ 500K. Magnetization measurements confirm these values through jumps at \textit{T$_c$} in the zero field cooled curves, and by the occurrence diamagnetic hysteretic cycles shrinking with temperature. Our results open the door towards the study of above room temperature superconducting ill-stacked graphite phases.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Hg Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.1	Pressure not reported	unknown
CuO Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	77	Pressure not reported	unknown
HgBa2Ca2Cu3O8+x Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	166	26 GPa	unknown