Phonon-mediated superconductivity in transition-metal trioxides XO3 (X = Ru, Re, Os, Ir, Pt) under pressure

Aiqin Yang; Xiangru Tao; Yundi Quan; Peng Zhang

doi:10.1103/PhysRevB.110.174504

← Back to search

Phonon-mediated superconductivity in transition-metal trioxides XO3 (X = Ru, Re, Os, Ir, Pt) under pressure

Aiqin Yang, Xiangru Tao, Yundi Quan, Peng Zhang

arXiv:2410.18405 · DOI 10.1103/PhysRevB.110.174504 · 2024-10-24 · Physical Review B

T3experimental

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

A recent experiment by Shan {\it et al} [arXiv:2304.09011] found that rhenium trioxide ReO$_3$, a simple metal at the ambient pressure, becomes superconducting with a transition temperature as high as 17 K at 30 GPa. In this paper, we analyze the electron-phonon origin of superconductivity in rhombohedral ReO$_3$ in detail. In addition, we also conduct a high-throughout screening of isostructural transition-metal trioxides XO$_3$ in searching for potential pressure-induced superconductors. Totally twenty-eight XO$_3$ compounds have been studied, in which four candidates RuO$_3$, OsO$_3$, IrO$_3$ and PtO$_3$ are predicted superconducting with the transition temperatures of 26.4, 30.3, 0.9 and 2.8 K at 30 GPa, respectively. Both IrO$_3$ and PtO$_3$ stay superconducting even at the ambient pressure. In ReO$_3$, RuO$_3, $OsO$_3$ and IrO$_3$, the conduction electrons around the Fermi level are dominantly from the X-d and the O-2p orbitals, and their electron-phonon coupling originates from the lattice dynamics of both the heavier transition-metal-atom and the oxygen-atom. Inclusion of spin-orbital coupling would mildly suppress the transition temperatures of these transition-metal trioxide superconductors except RuO$_3$.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
ReO3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	17	30 GPa	unknown
RuO3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26.4	30 GPa	unknown
OsO3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30.3	30 GPa	unknown
IrO3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.9	30 GPa	unknown
PtO3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.8	30 GPa	unknown
IrO3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.4	Pressure unresolved	unknown
PtO3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1.5	Pressure unresolved	unknown
CaH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	220	150 GPa	unknown
CaH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	215	172 GPa	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	204	200 GPa	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	204	200 GPa	unknown
LaH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	274	210 GPa	unknown
LaH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	274	210 GPa	unknown
Mg2IrH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	160	Pressure unresolved	unknown
Mg2RhH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	50	Pressure unresolved	unknown
Al2MnH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	50	Pressure unresolved	unknown
Li2CuH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	50	Pressure unresolved	unknown
CaB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	50	Pressure unresolved	unknown
CaB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9.4	Pressure unresolved	unknown
NbB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9.2	Pressure unresolved	unknown
ScB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1.5	Pressure unresolved	unknown
MoB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	32	100 GPa	unknown