In-situ Investigation of the Phase Formation and Superconductivity in V$_3$Si Thin Films at High Temperatures

Manjith Bose; David L. Cortie; Sergey Rubanov; Anton P. Le Brun; Trevor R. Finlayson; Jeffrey C. McCallum

doi:10.1016/j.apsusc.2025.162930

← Back to search

In-situ Investigation of the Phase Formation and Superconductivity in V$_3$Si Thin Films at High Temperatures

Manjith Bose, David L. Cortie, Sergey Rubanov, Anton P. Le Brun, Trevor R. Finlayson, Jeffrey C. McCallum

arXiv:2412.04159 · DOI 10.1016/j.apsusc.2025.162930 · 2024-12-05 · Applied Surface Science

T1experimental2 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Vanadium silicide (V$_3$Si) is a promising superconductor for integration with silicon-based electronics, however the interfacial growth kinetics have a strong influence on the resulting superconducting properties and are not yet fully understood. In this study, we have used neutron reflectometry to reveal the phase transformation during thin film growth driven by different annealing strategies. We examined the silicide formation when a thin layer of vanadium undergoes reactive diffusion with a silicon dioxide film on silicon at temperatures from 650-800 °C. To further investigate the time evolution of different phases under various annealing temperatures, a chemical model was developed and subsequent simulations were performed. The results of this model were validated using X-ray diffraction and cross-sectional TEM analysis. Correlations were observed between the structure and superconducting properties. Over-annealing films leads to complete depletion of the SiO$_2$ barrier layer, forming diffuse interfaces and driving the formation of undesirable silicon-rich silicides. Avoiding this by controlling time and temperature, allows higher quality superconducting films to be achieved. The $T_c$ of the films was found to be 13 K, and the annealing conditions influenced the critical fields and the paramagnetic Meissner effect near $T_c$. For optimally-annealed films, superconducting order parameters were calculated. Ginzberg-Landau theory was applied to explain flux penetration.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
V3Si Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	13	Pressure not reported	onset
V3Si Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	17.1	Pressure not reported	unknown