Tuning the structure and superconductivity of SrNi$_2$P$_2$ by Rh substitution

Juan Schmidt, Aashish Sapkota, Carsyn L. Mueller, Shuyang Xiao, Shuyuan Huyan, Tyler J. Slade, Seok-Wook Lee, Sergey L. Bud'ko, Paul C. Canfield

arXiv:2412.09736 · 2024-12-12

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

SrNi$_2$P$_2$ is unique among the ThCr$_2$Si$_2$ class since it exhibits a temperature induced transition upon cooling from an uncollapsed tetragonal (ucT) state to a one-third-collapsed orthorhombic (tcO) state where one out of every three P-rows bond across the Sr layers. This compound is also known for exhibiting bulk superconductivity below 1.4 K at ambient pressure. In this work, we report on the effects of Rh substitution in Sr(Ni$_{1-x}$Rh$_x$)$_2$P$_2$ on the structural and superconducting properties. We studied the variation of the nearest P-P distances as a function of the Rh fraction at room temperature, as well as its temperature dependence for selected compositions. We find that increasing the Rh fraction leads to a decrease in the transition temperature between the ucT and tcO states, until a full suppression of the tcO state for $x\geq 0.166$. The superconducting transition first remains nearly insensitive to the Rh fraction, and then it increases to 2.3 K after the tcO state is fully suppressed. These results are summarized in a phase diagram, built upon the characterization by energy dispersive x-ray spectroscopy, x-ray diffraction, resistance, magnetization and specific heat measurements done on crystalline samples with varying Rh content. The relationship between band structure, crystal structure and superconductivity is discussed based on previously reported band structure calculations on SrRh$_2$P$_2$. Moreover, the effect of Rh fraction on the stress-induced structural transitions is also addressed by means of strain-stress studies done by uniaxial compression of single-crystalline micropillars of Sr(Ni$_{1-x}$Rh$_x$)$_2$P$_2$.

Source-reported materials — not catalogue approval

FormulaReported Tc (K)Pressure (GPa)Type
SrNi2P2

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

1.4Pressure unresolvedunknown
SrNi2P2

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

1.4Pressure unresolvedunknown
SrNi2P2

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

1.4Pressure unresolvedunknown
SrNi2P2

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

1.4Pressure not reportedunknown
Sr(1-x)Ba(x)Ni2P2

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

2.85Pressure not reportedunknown
BaNi2P2

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

2.5Pressure not reportedunknown

Similar papers