Guangdi Zhou; Wei Lv; Heng Wang; Zihao Nie; Yaqi Chen; Yueying Li; Haoliang Huang; Weiqiang Chen; Yujie Sun; Qi-Kun Xue; Zhuoyu Chen

doi:10.1038/s41586-025-08755-z

Ambient-pressure superconductivity onset above 40 K in bilayer nickelate ultrathin films

Guangdi Zhou, Wei Lv, Heng Wang, Zihao Nie, Yaqi Chen, Yueying Li, Haoliang Huang, Weiqiang Chen, Yujie Sun, Qi-Kun Xue, Zhuoyu Chen

arXiv:2412.16622 · DOI 10.1038/s41586-025-08755-z · 2024-12-21 · Nature

T1experimental165 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The discovery of bilayer nickelate superconductors under high pressure has opened a new chapter in high-transition temperature (high-TC) superconductivity. Here, we report ambient-pressure superconductivity onset above the McMillan limit (40 K) in bilayer nickelate epitaxial ultrathin films. Three-unit-cell (3UC) thick La2.85Pr0.15Ni2O7 single-phase-crystalline films are grown using the gigantic-oxidative atomic-layer-by-layer epitaxy (GOALL-Epitaxy) on SrLaAlO4 substrates. Resistivity measurements and magnetic-field responses indicate onset TC = 45 K. The transition to zero resistance exhibits characteristics consistent with a Berezinskii-Kosterlitz-Thouless (BKT)-like behavior, with TBKT = 9 K. Meissner diamagnetic effect is observed at TM = 8.5 K via a mutual inductance setup, in agreement with the BKT-like transition. In-plane and out-of-plane critical magnetic fields exhibit anisotropy. Scanning transmission electron microscopy (STEM) images and X-ray reciprocal space mappings (RSMs) show that the films maintain a tetragonal phase with coherent epitaxial compressive strain ~2% in the NiO2 planes relative to the bulk. Our findings pave the way for comprehensive investigations of nickelate superconductors under ambient pressure conditions and for exploring superconductivity at higher transition temperature through strain engineering in heterostructures.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
La2.85Pr0.15Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	45	Pressure unresolved	onset
La2.85Pr0.15Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9	Pressure unresolved	zero_resistance
La2.85Pr0.15Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.5	Pressure unresolved	onset