Prerequisite of superconductivity: SDW rather than tetragonal structure in double-layer La3Ni2O7-x
Shi, Mengzhu, Peng, Di, Li, Yikang, Xing, Zhenfang, Wang, Yuzhu, Fan, Kaibao, Li, Houpu, Wu, Rongqi, Zeng, Zhidan, Zeng, Qiaoshi, Ying, Jianjun, Wu, Tao, Chen, Xianhui
arXiv:2501.14202 · 2025-01-27
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The pressure-induced high-temperature superconductivity(Tc) in nickelates La3Ni2O7-x has sparked significant interest to explore its superconductivity at ambient pressure.Lan+1NinO3n+1(n=2,3)adopts an orthorhombic structure with tilted NiO6 octahedra and undergoes a spin-density-wave(SDW) transition at ambient pressure, while the octahedral tilting and the SDW are suppressed by pressure, and high pressure induces a structural transition from orthorhombic to tetragonal, and the high-Tc superconductivity is achieved in the tetragonal structure. This tetragonal structure is widely believed to be crucial for the pressure-induced superconductivity. Whether the pressure-stabilized tetragonal structure is a prerequisite for achieving nickelate superconductivity at ambient pressure is under hot debate. Here, by post-annealing of the orthorhombic La3Ni2O7-x as grown microcrystals with noticeable oxygen defects in high oxygen pressure environment, tetragonal La3Ni2O6.96 single crystals are successfully obtained at ambient pressure. In contrast to the orthorhombic La3Ni2O7-x, the tetragonal La3Ni2O7-x exhibits metallic behavior without a SDW transition at ambient pressure. Moreover, no superconductivity is observed at high pressure up to ~ 70 GPa. On the other hand, by utilizing Helium as the pressure medium, we have revisited the superconducting structure in pressurized orthorhombic La3Ni2O6.93. Our results indicate that the orthorhombic structure is quite robust against pressure, and no structural transition from orthorhombic to tetragonal happens, and the superconductivity under high pressure is achieved in orthorhombic structure rather than tetragonal structure claimed previously. All these results suggest that tetragonal structure is not prerequisite for achieving superconductivity in La3Ni2O7-x.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| La3Ni2O6.93 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Absence of superconductivity and density-wave transition in ambient-pressure tetragonal LaNiO
similarity 0.94Mengzhu Shi et al. · 2025 · arXiv:2501.12647
Source status unknown — claims are unverified
Stabilization of Tetragonal Phase and Aluminum-Doping Effect in a Bilayer Nickelate
similarity 0.90Jia-Yi Lu et al. · 2025 · arXiv:2511.21315
Source status unknown — claims are unverified
Electronic structure, self-doping, and superconducting instability in the alternating single-layer trilayer stacking nickelates La3Ni2O7
similarity 0.88Yang Zhang et al.
Source status unknown — claims are unverified
Structural transitions, octahedral rotations, and electronic properties of NiO rare-earth nickelates under high pressure
similarity 0.88Benjamin Geisler et al. · 2023 · arXiv:2309.15078
Source status unknown — claims are unverified
Optical control of the crystal structure in the bilayer nickelate superconductor La3Ni2O7 via nonlinear phononics
similarity 0.88Shu Kamiyama et al. · 2025 · arXiv:2501.11377
Source status unknown — claims are unverified
Heterostructuring as Gateway to Electron Doping of Nickelate Superconductors
similarity 0.87Chao Deng et al. · 2026 · arXiv:2607.08553
Source status unknown — claims are unverified