Damage of bilayer structure in La3Ni2O7-d induced by high pO2 annealing
Yulin Zhang, Cuiying Pei, Ning Guo, Longlong Fan, Mingxin Zhang, Lingzhen Wang, Gongting Zhang, Feiyu Li, Yunong Wang, Chao Ma, Wenyong Cheng, Shanpeng Wang, Qiang Zheng, Yanpeng Qi, Junjie Zhang
arXiv:2502.01501 · DOI 10.1016/j.jssc.2025.125757 · 2025-02-03
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The discovery of superconductivity with onset temperature of ~80 K in pressurized bilayer Ruddlesden-Popper La3Ni2O7-d has attracted much attention. Despite intense research, determination of the exact oxygen content and understanding of the relationship between superconductivity and oxygen content remain a big challenge. Here, we report a systematical study on the structure and physical properties of La3Ni2O7-d polycrystalline powders which were prepared using sol-gel method at ambient pressure and then annealed under various oxygen pressure. We found that high pO2 annealing with slow cooling results in a new phase, which can be modeled using the hybrid single-layer-trilayer La3Ni2O7 or the tetragonal bilayer La3Ni2O7. Scanning transmission electron microscopy (STEM) measurements revealed significant single layers and trilayers after high oxygen pressure annealing, evidencing damage of the bilayer structure. The superconducting transition under high pressure became weak for high pO2 annealed samples, which is consistent with the damage of the bilayer structure. Our results reveal that the bilayer structure is fragile and post-annealing under near atmosphere pressure of oxygen is suitable to maintain bilayer structure and increase oxygen content at the same time.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| La3Ni2O7-d Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 80 | Pressure not reported | onset |
Similar papers
Regulating oxygen content and superconductivity in LaNiO
similarity 0.90Peiyue Ma et al. · 2026 · arXiv:2605.04562
Source status unknown — claims are unverified
The evolution of pairing correlation with electron filling in a bilayer two-orbital model for LaNiO
similarity 0.89Y. F. Chen et al. · 2026 · arXiv:2605.25654
Source status unknown — claims are unverified
Superconductivity in monolayer-trilayer phase of LaNiO under high pressure
similarity 0.89Chaoxin Huang et al. · 2025 · arXiv:2510.12250
Source status unknown — claims are unverified
Interstitial oxygen order and its competition with superconductivity in LaPrNiO
similarity 0.89Zehao Dong et al. · 2025 · arXiv:2508.03414
Source status unknown — claims are unverified
Stabilizing and Tuning Superconductivity in LaNiO Films: Oxygen Recycling Protocol Reveals Hole-Doping Analogue
similarity 0.89Lifen Xiang et al. · 2025 · arXiv:2508.11581
Source status unknown — claims are unverified
Electronic reconstruction and interface engineering of emergent spin fluctuations in compressively strained LaNiO on SrLaAlO(001)
similarity 0.89Benjamin Geisler et al. · 2025 · arXiv:2503.10902
Source status unknown — claims are unverified