Superconducting LaPtH$_{ 6 }$ with triatomic hydrogen units

T. Ishikawa; Y. Tanaka; S. Tsuneyuki

Superconducting LaPtH$_{ 6 }$ with triatomic hydrogen units

T. Ishikawa, Y. Tanaka, S. Tsuneyuki

arXiv:2502.06821 · 2025-02-05

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

To veryfy "hot supreconductivity" recently proposed in lanthanum hydride-based compounds, we explored thermodynamically stable and superconducting phases in the lanthanum (La)-platinum (Pt)-hydrogen (H) ternary system at 20 GPa using an evolutionary construction scheme of a formation-enthalpy convex hull, universal neural network potential calculations, and density functional theory calculations. Although we found no evidence of the hot superconductivity in this ternary system, we predicted a unique compound, LaPtH$_{ 6 }$, which has equilateral triangular H$_{ 3 }$ units nearly forming a two-dimensional kagome lattice between La and Pt layers and shows the superconductivity at 18.67 K. This structure is dynamically stable from ambient pressure to at least 200 GPa and the superconducting critical temperature increases from 13.51 to 40.63 K.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
LaPtH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	18.67	20 GPa	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	203	155 GPa	unknown
LaH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	255	180 GPa	unknown
Li2MgH16 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	475	250 GPa	unknown
CSH7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	145	150 GPa	unknown
La2Pt2H13 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	11.46	20 GPa	unknown
La2Pt2H11 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9.98	20 GPa	unknown
LaPtH5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	6.56	20 GPa	unknown
La2Pt3H9 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	6.38	20 GPa	unknown
La4Pt6H17 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.58	20 GPa	unknown
La2Pt3H8 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.52	20 GPa	unknown
La4Pt6H15 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	6.4	20 GPa	unknown
LaPt2H7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	14.59	20 GPa	unknown
LaPt3H9 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	14.61	20 GPa	unknown
La4Pt2H13 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.98	20 GPa	unknown