Removal of excess iron by annealing processes and emergence of bulk superconductivity in sulfur-substituted FeTe

Ryosuke Kurihara; Ryusuke Kogure; Tomotaka Ota; Yuto Kinoshita; Satoshi Hakamada; Masashi Tokunaga; Hiroshi Yaguchi

Removal of excess iron by annealing processes and emergence of bulk superconductivity in sulfur-substituted FeTe

Ryosuke Kurihara, Ryusuke Kogure, Tomotaka Ota, Yuto Kinoshita, Satoshi Hakamada, Masashi Tokunaga, Hiroshi Yaguchi

arXiv:2502.09945 · 2025-02-14

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

There are several strategies to discover new superconductors. Growing new materials and applying high pressures can be the classic ways since superconductivity was found. Also, chemical processing, such as annealing, is another way to induce superconductivity in a non-superconducting material. Here, we show chemical processing effects in the non-superconducting material, sulfur-substituted FeTe. It has been known that superconductivity in S-substituted FeTe is induced by O$_2$ annealing. We revealed that hydrochloric acid etching and vacuum annealing for O$_2$-annealed samples made the quality of superconductivity higher by several physical property measurements. Furthermore, we visualized the superconducting regions by a magneto-optical imaging technique, indicating that the superconductivity in the processed sample was bulk. In this sample, we confirmed that the concentration of excess iron was reduced compared to that in the as-grown state. These results provide an important route to bulk superconductivity in S-substituted FeTe and its related iron-based compounds.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Fe1+yTe1-xSx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8	Pressure not reported	unknown
Fe1.096Te0.912S0.088 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8	Pressure not reported	onset
Fe1.096Te0.912S0.088 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8	Pressure not reported	onset
Fe1.096Te0.912S0.088 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.1	Pressure not reported	onset
Fe1.096Te0.912S0.088 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.4	Pressure not reported	onset
Fe1.096Te0.912S0.088 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.6	Pressure not reported	onset
Fe1.096Te0.912S0.088 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.6	Pressure not reported	onset