Impact of Pressure and Apical Oxygen Vacancies on Superconductivity in La$_3$Ni$_2$O$_7$

Chen Lu; Ming Zhang; Zhiming Pan; Congjun Wu; Fan Yang

doi:10.1038/s42005-025-02266-z

← Back to search

Impact of Pressure and Apical Oxygen Vacancies on Superconductivity in La$_3$Ni$_2$O$_7$

Chen Lu, Ming Zhang, Zhiming Pan, Congjun Wu, Fan Yang

arXiv:2502.14324 · DOI 10.1038/s42005-025-02266-z · 2026-01-05

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The bilayer nickelate La$_3$Ni$_2$O$_7$ under pressure has recently emerged as a promising system for high-$T_c$ superconductivity. In this work, we investigate the fate of the superconducting properties in La$_3$Ni$_2$O$_{7}$ under pressure, focusing on the effects of structural deformation and apical oxygen vacancies. Employing a low-energy effective $t$-$J_{\parallel}$-$J_{\perp}$ model for the $3d_{x^2-y^2}$ orbitals within the slave-boson mean-field approach, we demonstrate that the pairing strength is significantly enhanced in the high-pressure tetragonal $I4/mmm$ phase compared to the ambient pressure orthorhombic $Amam$ phase. Furthermore, by simulating random configurations of apical oxygen vacancies, we show that oxygen vacancies suppress both pairing strength and superfluid density. These results underscore the critical role of pressure and oxygen stoichiometry in tuning the SC of La$_3$Ni$_2$O$_7$, providing key insights into optimizing its high-$T_c$ behavior.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
La3Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	80	14 GPa	unknown
La3Ni2O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	40	Pressure unresolved	unknown
La4Ni3O10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	20	Pressure not reported	unknown
La5Ni3O11 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	60	Pressure not reported	unknown