Synthesis of Y$_3$Fe$_4$H$_{20}$ as a new prototype structure for ternary superhydrides recoverable at ambient pressure

M. Caussé; L. Toraille; G. Geneste; P. Loubeyre

← Back to search

Synthesis of Y$_3$Fe$_4$H$_{20}$ as a new prototype structure for ternary superhydrides recoverable at ambient pressure

M. Caussé, L. Toraille, G. Geneste, P. Loubeyre

arXiv:2505.16799 · 2025-05-22

T2experimental1 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Reaching pressures in the 100 GPa range enables the synthesis of hydrogen-rich compounds, with nontraditional H stoichiometries and H sublattices, called superhydrides. Record-breaking superconductivity temperature in some superhydrides have attracted great interest. A crucial next step is to stabilize superhydrides outside of high-pressure environments, leading to a search beyond binary hydrides to ternary hydrides. Here, we report the synthesis of Y$_3$Fe$_4$H$_{20}$ at pressures starting at 60 GPa by compressing an hydrogenated Y-Fe compound, embedded in hydrogen in a laser-heated diamond anvil cell. Single-crystal X-ray diffraction allowed us to resolve the Y$_3$Fe$_4$ lattice skeleton, and a constrained ab initio structural search was used to position the hydrogen atoms. FeH$_8$ cubic molecular units form building blocks which are connected edge-to-edge by sharing two hydrogen atoms, creating a framework that hosts Y cations. Remarkably, Y$_3$Fe$_4$H$_{20}$ maintains its structure through decompression, making it the first superhydride recovered metastable under ambient conditions.