Enhancement of hydrogen absorption and hypervalent metal hydride formation in lanthanum using cryogenic ball milling
Sakun Duwal, Vitalie Stavila, Catalin Spataru, Mohana Shivanna, Portia Allen, Timothy Elmslie, Christopher T. Seagle, Jason Jeffries, Nenad Velisavljevic, Jesse Smith, Paul Chow, Yuming Xiao, Maddury Somayazulu, Peter A. Sharma
arXiv:2506.23980 · 2025-06-30
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Rare earth superhydrides exhibit high temperature superconductivity but are difficult to characterize and use in applications due to their high formation and stability pressures, which are typically in excess of 100 GPa. We studied how modification of the rare earth precursor improves hydrogen reactivity and hydrogen uptake for forming such metal hydrides at lower pressures. An elemental lanthanum precursor was milled at liquid nitrogen temperatures for different time intervals. After exposure to gaseous hydrogen at 380 C and 100 bar, we found a systematic enhancement of hydrogen absorption with increasing ball milling time for forming the LaHx, x=2-3 phase. Exposing the precursor to pressures up to 60 GPa with an ammonia borane (BNH6) hydrogen source resulted in a hypervalent LaH4 phase. This LaH4 phase is associated with the suppression of a rhombohedral distortion of the Fm3-m cubic structure after cryomilling the precursor.
Similar papers
Imaging magnetic flux trapping in lanthanum hydride using diamond quantum sensors
similarity 0.86Yang Chen et al. · 2025 · arXiv:2510.21877
Source status unknown — claims are unverified
Long-Term Stability of Superconducting Metal Superhydrides
similarity 0.86Vasily S. Minkov et al. · 2025 · arXiv:2507.08009
Source status unknown — claims are unverified
Road to Room-Temperature Superconductivity: Tc above 260 K in Lanthanum Superhydride under Pressure
similarity 0.86Russell J. Hemley et al. · 2019 · arXiv:1906.03462
Source status unknown — claims are unverified
Raman fingerprint of high-temperature superconductivity in compressed hydrides
similarity 0.84Philip Dalladay-Simpson et al. · 2025 · arXiv:2511.10784
Source status unknown — claims are unverified
Computational materials discovery for lanthanide hydrides at high pressure for high temperature superconductivity
similarity 0.84Evgeny Plekhanov et al.
Source status unknown — claims are unverified
Prediction of high-Tc conventional superconductivity in the ternary lithium borohydride system
similarity 0.84Christian Kokail et al.
Source status unknown — claims are unverified