High-performance amorphous superconducting rhenium films by e-beam evaporation

E. V. Tarkaeva; V. A. Ievleva; A. R. Prishchepa; E. S. Zhukova; A. V. Terentiev; A. Yu. Kuntsevich

doi:10.1063/5.0292196

← Back to search

High-performance amorphous superconducting rhenium films by e-beam evaporation

E. V. Tarkaeva, V. A. Ievleva, A. R. Prishchepa, E. S. Zhukova, A. V. Terentiev, A. Yu. Kuntsevich

arXiv:2507.13536 · DOI 10.1063/5.0292196 · 2025-07-17 · Journal of Applied Physics

T4experimental2 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We present electron beam evaporation of rhenium films on room-temperature substrates. The films are shown to be amorphous and achieve a record-high critical temperature for rhenium - exceeding 7 K at the midpoint of the transition - alongside a high critical current density of 5000 A/mm^2 and critical fields above 10 T. Terahertz spectroscopy reveals a BCS-like character of superconductivity with a zero-temperature energy gap of approximately 2 meV and subgap optical conductivity. Despite being friable, the films are stable and compatible with lift-off processes that opens the capabilities for superconducting device applications.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Re Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7	Pressure not reported	midpoint
Re Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8	Pressure not reported	onset
Re Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Tc Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.2	Pressure not reported	unknown
Pb Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7.2	Pressure not reported	unknown
Nb Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9.25	Pressure not reported	unknown
Ta Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.5	Pressure not reported	unknown
Al Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1.1	Pressure not reported	unknown
Al Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	6	Pressure not reported	unknown
Re Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	1.7	Pressure not reported	unknown
Re Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	3	Pressure not reported	unknown
Re Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7	Pressure not reported	unknown
Re Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	6	Pressure not reported	unknown
Re Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	3	Pressure not reported	unknown