Same-group element replacement enhances superconductivity in clathrate-like YH4

Xuejie Li; Yuzhou Hao; Yujie Liu; Xiaoying Wang; Turab Lookman; Jun Sun; Xiangdong Ding; Zhibin Gao

doi:10.1063/5.0271662

← Back to search

Same-group element replacement enhances superconductivity in clathrate-like YH4

Xuejie Li, Yuzhou Hao, Yujie Liu, Xiaoying Wang, Turab Lookman, Jun Sun, Xiangdong Ding, Zhibin Gao

arXiv:2509.17501 · DOI 10.1063/5.0271662 · 2025-09-22 · The Journal of chemical physics

T3experimental

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

H3S, LaH10, and hydrogen-based compounds have garnered significant interest due to their high-temperature superconducting properties. However, the requirement for extremely high pressures limits their practical applications. In this study, YH4 is adopted as a base material, with partial substitution of Yttrium (Y) by Scandium (Sc), Lanthanum (La), and Zirconium (Zr). Pure YH4, stable at 120 GPa, exhibits a critical temperature (Tc) of 84-95 K. Substituting half of the Y atoms increases Tc to 124.43 K for (Y,Sc)H4 at 100 GPa but reduces it to 101.24 K for (Y,La)H4 at 120 GPa. In contrast, (Y,Zr)H4 at 200 GPa shows a further suppressed Tc of 69.55 K. The remarkable superconductivity in (Y,Sc)H4 might be related to its unique phonon dispersion without optical-acoustic gap, compressed Y-H bonds, and significant electron delocalization under pressure, collectively boosting electron-phonon interactions. Furthermore, the lowest optical phonons play a crucial role in the superconductivity of these materials. This work suggests that substituting Y with same-group metal elements is an effective strategy to enhance Tc in hydride superconductors.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
(Y,Sc)H4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	124.43	100 GPa	unknown
(Y,La)H4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	101.24	120 GPa	unknown
(Y,Zr)H4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	69.55	200 GPa	unknown
YH4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	88	155 GPa	unknown
YH4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	89.5	120 GPa	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	203	90 GPa	unknown
LaH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	250	170 GPa	unknown
YH9 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	243	201 GPa	unknown
YH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	224	166 GPa	unknown
YH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	315.5	250 GPa	unknown
CaYH12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	258	200 GPa	unknown
YCaH12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	230	180 GPa	unknown
MoB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	37	90 GPa	unknown
MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	100	Pressure not reported	unknown
(La,Ce)H9 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	176	100 GPa	unknown