Three-Dimensional Niobium Coaxial Cavity with $\sim0.1\,$second Lifetime
Takaaki Takenaka, Takayuki Kubo, Imran Mahboob, Kosuke Mizuno, Hitoshi Inoue, Takayuki Saeki, Shiro Saito
arXiv:2510.01819 · 2025-10-02
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report on the internal quality factor of a three-dimensional niobium quarter-wave coaxial cavity, with mid-temperature annealing, exhibiting $Q_{\rm int} \gtrsim 3\times10^9$ at the single-photon level below 20\,mK, which corresponds to an internal photon lifetime of $τ_{\rm int}\sim90\,\mathrm{ms}$. Moreover, $Q_{\rm int}$ of the mid-temperature annealed cavities remains almost unchanged even after several cooldown cycles and air exposure. These results suggest that stable low-loss niobium oxides might be formed by mid-temperature annealing on the surface of three-dimensional niobium cavity. This surface treatment could be applicable to the fabrication of 2D superconducting circuits and help improve the lifetime of Nb-based superconducting qubits.
Similar papers
Insight into bulk niobium superconducting RF cavities performances by tunneling spectroscopy
similarity 0.88N. R. Groll et al. · 2018 · arXiv:1805.06359
Source status unknown — claims are unverified
Materials and devices for fundamental quantum science and quantum technologies
similarity 0.88Marco Polini et al. · 2022 · arXiv:2201.09260
Source status unknown — claims are unverified
Signatures of Enhanced Superconducting Properties in Niobium Cavities
similarity 0.88D. Bafia et al. · 2021 · arXiv:2103.10601
Source status unknown — claims are unverified
Three-dimensional superconducting resonators at mK with the photon lifetime up to seconds
similarity 0.87A. Romanenko et al. · 2018 · arXiv:1810.03703
Source status unknown — claims are unverified
Understanding Quality Factor Degradation in Superconducting Niobium Cavities at Low Microwave Field Amplitudes
similarity 0.87A. Romanenko & D. I. Schuster · 2017 · arXiv:1705.05982
Source status unknown — claims are unverified
Improvement and protection of niobium surface superconductivity by Atomic Layer Deposition and heat treatment
similarity 0.87T. Proslier et al. · 2008 · arXiv:0808.3427
Source status unknown — claims are unverified