Higher-order epitaxy: A pathway to suppressing structural instability and emergent superconductivity

Yuki Sato, Soma Nagahama, Shunsuke Kitou, Hajime Sagayama, Ilya Belopolski, Ryutaro Yoshimi, Minoru Kawamura, Atsushi Tsukazaki, Naoya Kanazawa, Takuya Nomoto, Ryotaro Arita, Taka-hisa Arima, Masashi Kawasaki, Yoshinori Tokura

arXiv:2510.07947 · DOI 10.1038/s41467-025-65902-w · 2025-10-09 · Nature Communications

T4experimental1 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Molecular beam epitaxy enables the growth of thin film materials with novel properties and functionalities. Typically, the lattice constants of films and substrates are designed to match to minimise disorders and strains. However, significant lattice mismatches can result in higher-order epitaxy, where commensurate growth occurs with a period defined by integer multiples of the lattice constants. Despite its potential, higher-order epitaxy is rarely used to enhance material properties or induce emergent phenomena. Here, we report single-crystalline FeTe films grown via 6:5 commensurate higher-order epitaxy on CdTe(001) substrates. Scanning transmission electron microscopy reveals self-organised periodic interstitials near the interface, arising from higher-order lattice matching. Synchrotron x-ray diffraction shows that the tetragonal-to-monoclinic structural transition in bulk FeTe is strongly suppressed. Remarkably, these films exhibit substrate-selective two-dimensional superconductivity, likely due to suppressed monoclinic distortion. These findings demonstrate the potential of higher-order epitaxy as a tool to control materials and inducing emergent phenomena.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	10	Pressure not reported	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
FeTe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	12	Pressure not reported	onset