Metal hydrides achieve high-Tc superconductivity at low pressure by mimicking high-pressure H3S chemical bonding
Wendi Zhao, Shumin Guo, Chengda Li, Abhiyan Pandit, Tian Cui, Defang Duan, Maosheng Miao
arXiv:2602.13584 · 2026-02-14
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Compressed hydrides are promising candidates for high-temperature superconductivity, yet achieving simultaneous structural stability and high-Tc at low pressures remains challenging. Here, we introduce a new mechanism for accomplishing this goal by mimicking the bonding characteristics of high-pressure H3S within metal hydrides. Using Li3CuH4 as an example, its Cu-H covalent interaction effectively mimics the core function of the S-H bonding in H3S. This interaction not only induces a high hydrogen-derived electronic density of states at the Fermi level, but also softens the hydrogen phonon modes, thereby significantly enhancing the electron-phonon coupling. Furthermore, embedding the strongly ionic Li3H lattice into the covalent Cu-H framework stabilizes the structure at significantly low pressures via a chemical-template effect, while maintaining high-Tc. Li3CuH4 exhibits excellent thermodynamic stability at 20 GPa, with a Tc of 39.25 K at 12 GPa. Further comprehensive high-throughput studies on Li3MH4 (M = transition metal) compounds uncover general principles applicable to a broader range of compounds. This work establishes a new paradigm for the simultaneous optimization of the stability and high-temperature superconductivity of metal hydrides through complementary sublattice interactions, thus advancing the search for practical and viable superconducting materials.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Li3CuH4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 39.25 | 12 GPa | unknown |
Similar papers
Route to high-Tc superconductivity via CH4-intercalated H3S hydride perovskites
similarity 0.90Wenwen Cui et al.
Source status unknown — claims are unverified
High-Tc superconductivity above 130 K in cubic MH4 compounds at ambient pressure
similarity 0.90Xinxin Li et al. · 2025 · arXiv:2511.04222
Source status unknown — claims are unverified
Superconductivity of electron-doped chalcohydrides under high pressure
similarity 0.89Yu Du et al.
Source status unknown — claims are unverified
High-temperature superconductivity in M2BH6 hydrides under near ambient pressure
similarity 0.89Weiguo Sun et al.
Source status unknown — claims are unverified
Compressed hydrides as metallic hydrogen superconductors
similarity 0.89Yundi Quan et al.
Source status unknown — claims are unverified
Underlying mechanism of charge transfer in Li-doped MgH at high pressure
similarity 0.88Chongze Wang et al. · 2020 · arXiv:2007.03914
Source status unknown — claims are unverified