Tuning of superconducting properties with disorder in NbxSn nanocrystalline thin films

Mahesh Poojary; Vishwanadh Bathula; Yash Kumar; Amar Verma; Ekta Kadam; Sangita Bose

doi:10.1016/j.jallcom.2026.186937

← Back to search

Tuning of superconducting properties with disorder in NbxSn nanocrystalline thin films

Mahesh Poojary, Vishwanadh Bathula, Yash Kumar, Amar Verma, Ekta Kadam, Sangita Bose

arXiv:2603.00954 · DOI 10.1016/j.jallcom.2026.186937 · 2026-03-01 · Journal of Alloys and Compounds

T3experimental

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Nanocrystalline superconducting films offer an excellent platform to explore the interplay between disorder, granularity, and dimensionality. In this work, we investigate two series of NbxSn thin films with near-stoichiometric (x =3) and slightly Sn-rich (x =2.5) compositions, deposited on Si (100) substrates via DC magnetron sputtering. Both series exhibit nanocrystalline morphology, with the Sn-rich films displaying smaller grain sizes and a more granular microstructure. A suppression of the superconducting transition temperature (Tc) with decreasing film thickness is observed in both series. Notably, a disorder-driven crossover to an insulating state emerges, occurring at a thickness of approximately 11 nm for the Sn-rich films-about twice that of the stoichiometric films. The estimated disorder parameter (kFl=0.4) in the thinnest films indicates proximity to the Anderson localization regime for these films. Magneto-transport measurements reveal a thickness-driven 3D to 2D crossover, with its onset strongly dependent on film stoichiometry. Furthermore, a pronounced suppression of superfluid stiffness is observed in the Sn-rich films, corroborating the structure-property correlations identified in this study. This work highlights the role of stoichiometry controlled disorder in tuning superconductivity in granular NbxSn thin films.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Nb3Sn Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Nb2.5Sn Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown