Uniaxial Compression-Induced Anisotropy and Electronic Dimensionality in the Iron-Based Superconductor FeSe

Alexy Bertrand; Masaki Mito; Kazuma Nakamura; Mahmoud Abdel-Hafiez

← Back to search

Uniaxial Compression-Induced Anisotropy and Electronic Dimensionality in the Iron-Based Superconductor FeSe

Alexy Bertrand, Masaki Mito, Kazuma Nakamura, Mahmoud Abdel-Hafiez

arXiv:2604.01062 · 2026-04-01

T2theoretical

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The evolution of the superconducting transition temperature ($T_c$) in FeSe was investigated under in-plane, out-of-plane, and hydrostatic compression. For pressures up to 0.6 GPa, $T_c$ increases regardless of the compression mode, consistent with the suppression of nematic ordering. However, once nematicity is suppressed, $T_c$ exhibits a striking directional dependence: out-of-plane compression shows behavior similar to the hydrostatic case, with a sharp increase in $T_c$, whereas in-plane compression suppresses superconductivity. First-principles calculations suggest that in-plane compression shifts a hybridized band of Se $p_z$ and Fe $d_{x^2-y^2}$ character so that it crosses the Fermi level along the $Γ$-Z direction, leading to the emergence of an additional metallic band. This leads to an increased three-dimensionality of the electronic structure and may be interpreted as a possible Lifshitz-type change in the Fermi surface.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9	Pressure not reported	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	13	0.8 GPa	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	10	1.2 GPa	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	38.3	6 GPa	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9.8	Pressure unresolved	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	12	0.5 GPa	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	10.2	1.1 GPa	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	24	2.74 GPa	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	21	2.88 GPa	unknown