Enhancement of $J$$_c$ by Proton Irradiation in HgBa$_2$Ca$_2$Cu$_3$O$_8$$_+$$_δ$ Single Crystals

Wenjie Li; Ran Guo; Xin Zhou; Qiang Hou; Mengqin Liu; Longfei Sun; Yuhang Zu; Wenshan Hong; Yuan Li; Sheng Li; Yue Sun; Zhixiang Shi; Tsuyoshi Tamegai

doi:10.1088/1361-6668/ae6c9c

Enhancement of $J$$_c$ by Proton Irradiation in HgBa$_2$Ca$_2$Cu$_3$O$_8$$_+$$_δ$ Single Crystals

Wenjie Li, Ran Guo, Xin Zhou, Qiang Hou, Mengqin Liu, Longfei Sun, Yuhang Zu, Wenshan Hong, Yuan Li, Sheng Li, Yue Sun, Zhixiang Shi, Tsuyoshi Tamegai

arXiv:2605.05800 · DOI 10.1088/1361-6668/ae6c9c · 2026-05-07

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Critical current density is the key parameter for the practical application of superconductivity. In this study, 3 MeV proton irradiation experiments were conducted on HgBa$_2$Ca$_2$Cu$_3$O$_8$$_+$$_δ$ single crystals to introduce pinning centers. The critical current density is found to be strongly enhanced after the irradiation with its maximum at a dose of 1$\times$10$^{16}$/cm$^2$, where the self-field critical current density at 2 K is enhanced from 5.5 MA/cm$^2$ to 26 MA/cm$^2$. At 77 K, the self-field critical current density for all irradiated crystals is over 0.1 MA/cm$^2$. The power-law dependence of the critical current density on the magnetic field is observed after irradiation, with a large power-law exponent $α$ close to 1. A monotonic magnetic field dependence of the normalized magnetic relaxation rate is observed, which could be attributed to the low irreversibility field caused by the large anisotropy in Hg1223 single crystals. Through the analysis of the pinning force density of the crystal before and after irradiation, a clear mechanism change has been observed.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
HgBa2Ca2Cu3O8+δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	129	Pressure not reported	onset
HgBa2Ca2Cu3O8+x Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	133	Pressure not reported	unknown
SmFeAsO0.63H0.37 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	46	Pressure not reported	unknown
Nb3Sn Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	16	Pressure not reported	unknown
YBa2Cu3O8+x Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	91	Pressure not reported	unknown
NbTi Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9.6	Pressure not reported	unknown
Bi2Sr2CaCu2Ox Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	89	Pressure not reported	unknown
Ba0.6K0.4Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	28	Pressure not reported	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9	Pressure not reported	unknown