Microstructure and superconducting properties of hot isostatically pressed MgB2
T C Shields, K Kawano, D Holdom, J S Abell
arXiv:cond-mat/0107034 · DOI 10.1088/0953-2048/15/2/303 · 2001-07-02 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Bulk samples of MgB2 have been formed by hot isostatic pressing (HIPping) of commercial powder at 100MPa and 950=B0C. The resulting material is 100% dense with a sharp superconducting transition at 37.5K. Microstructural studies have indicated the presence of small amounts of second phases within the material, namely MgO and B rich compositions, probably MgB4. Magnetisation measurements performed at 20K have revealed values of Jc=1.3 x 106A/cm2 at zero field, and 9.3 x 105A/cm2 at 1T. Magneto optical (MO) studies have shown direct evidence for the superconducting homogeneity and strong intergranular current flow in the material.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 37.5 | Pressure unresolved | unknown |
Similar papers
Effects of pressure on the superconducting properties of magnesium diboride
similarity 0.89X. J. Chen et al. · 2002 · arXiv:cond-mat/0203195
Source status unknown — claims are unverified
High-pressure high-temperature solution growth, structural, and superconducting properties of Fe-substituted MgB2 single crystals
similarity 0.88N. D. Zhigadlo & R. Puzniak · 2025 · arXiv:2505.16432
Source status unknown — claims are unverified
Novel magnesium borides and their superconductivity
similarity 0.87M. M. Davari Esfahani et al. · 2017 · arXiv:1702.02221
Source status unknown — claims are unverified
Structural features, stacking faults, and grain boundaries in MgB2 superconducting materials
similarity 0.87J. Q. Li et al. · 2001 · arXiv:cond-mat/0104350
Source status unknown — claims are unverified
High-pressure synthesis of pure and doped superconducting MgB2 compounds
similarity 0.87P. Toulemonde et al. · 2002 · arXiv:cond-mat/0207033
Source status unknown — claims are unverified
In-situ Magnesium Diboride Superconducting Thin Films grown by Pulsed Laser Deposition
similarity 0.86G. Grassano et al. · 2001 · arXiv:cond-mat/0103572
Source status unknown — claims are unverified