Superconductivity in the Chalcogens up to Multimegabar Pressures

Eugene Gregoryanz; Viktor V. Struzhkin; Russell J. Hemley; Mikhail I. Eremets; Ho-kwang Mao; Yuri A. Timofeev

doi:10.1103/PhysRevB.65.064504

← Back to search

Superconductivity in the Chalcogens up to Multimegabar Pressures

Eugene Gregoryanz, Viktor V. Struzhkin, Russell J. Hemley, Mikhail I. Eremets, Ho-kwang Mao, Yuri A. Timofeev

arXiv:cond-mat/0108267 · DOI 10.1103/PhysRevB.65.064504 · 2001-08-17 · Physical Review B

T2theoretical50 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Highly sensitive magnetic susceptibility techniques were used to measure the superconducting transition temperatures in S up to 231($\pm$5) GPa. S transforms to a superconductor with T$_c$ of 10 K and has a discontinuity in T_c dependence at 160 GPa corresponding to bco to beta-Po phase transition. Above this pressure T_c in S has a maximum reaching about 17.3(+/-0.5) K at 200 GPa and then slowly decreases with pressure to 15 K at 230 GPa. This trend in the pressure dependence parallels the behavior of the heavier members Se and Te. Superconductivity in Se was also observed from 15 to 25 GPa with T_c changing from 4 to 6 K and above 150 GPa with T_c of 8 K. Similiarities in the T_c dependences for S, Se, and Te, and the implications for oxygen are discussed.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Se Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4	15 GPa	unknown
Se Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	6	25 GPa	unknown
Se Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8	150 GPa	unknown
Te Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	4 GPa	unknown
Te Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	35 GPa	unknown
Se Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	17 GPa	unknown
Se Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	140 GPa	unknown