Preparation and Characterization of Homogeneous YBCO Single Crystals with Doping Level near the SC-AFM Boundary

Ruixing Liang; D. A. Bonn; W. N. Hardy; Janice C. Wynn; K. A. Moler; L. Lu; S. Larochelle; L. Zhou; M. Greven; L. Lurio; S. G. J. Mochrie

doi:10.1016/S0921-4534(02)01269-8

Preparation and Characterization of Homogeneous YBCO Single Crystals with Doping Level near the SC-AFM Boundary

Ruixing Liang, D. A. Bonn, W. N. Hardy, Janice C. Wynn, K. A. Moler, L. Lu, S. Larochelle, L. Zhou, M. Greven, L. Lurio, S. G. J. Mochrie

arXiv:cond-mat/0111379 · DOI 10.1016/S0921-4534(02)01269-8 · 2001-11-20 · Physica C-superconductivity and Its Applications

T328 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

High-purity and homogeneous YBa2Cu3Oy single crystals with carrier doping level near the AFM-SC boundary have been obtained in the oxygen content range between y = 6.340 and 6.370. The crystals are ortho-II phase at room temperature and undergo the orthorhombic to tetragonal transition at about 140_Degree_C. They show sharp superconducting transitions, with Tc between 4 and 20 K. Tc changes by 0.8 K when the oxygen content y is changed by 0.001, and is also sensitive to annealing conditions near room temperature, due to the dependence of doping on oxygen ordering correlation lengths. Crystals with oxygen content y lower than 6.345 are non-superconducting.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
YBa2Cu3Oy Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4	Pressure not reported	unknown
YBa2Cu3Oy Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	20	Pressure not reported	unknown