Magnetic studies of Ca1-xMxRuO3 (M=La and Sr)
I. Felner, U. Asaf
arXiv:cond-mat/0204341 · DOI 10.1016/S0921-4526(03)00421-6 · 2002-04-16 · Physica B-condensed Matter
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
CaRuO3 is a perovskite with an orthorhombic distortion and shows the characteristics of spin-glass behavior below TC=87 K. The La3+ substitution for Ca2+ in Ca1-xLaxRuO3 samples, induces a disorder in the Ca site (the A site) and the system becomes antiferromagnetically (AFM) ordered with TN = 58 and 19 K for x=0.1 x=0.5 respectively. In the Ca1-xSrxRuO3 system, the Ca0.8Sr0.2RuO3 sample is canted-AFM ordered at 107 K. The compounds with higher Sr concentration display ferromagnetic behavior and the saturation moment increases with Sr. Huge magnetic hysteresis loops are obtained at low temperatures. The coercive field (HC) decreases with Sr. For x=0.4 HC =9.5 kOe (at 5 K) whereas for SrRuO3 HC =2.4 kOe. For x=0.4 and 0.6, HC decreases sharply with temperature and than increases again with a peak at 95 and 115 K, respectively. On the other hand, for SrRuO3, HC remains practically unchanged up to 50 K and shows a peak at 90 K and than decrease sharply up to TC =165 K.
Similar papers
Investigation of the ferromagnetic transition in the correlated 4d perovskites SrRuRhO
similarity 0.88K. Yamaura et al. · 2003 · arXiv:cond-mat/0311228
Source status unknown — claims are unverified
Electronic structure and magnetism in Ru based perovskites
similarity 0.88I. I. Mazin & D. J. Singh · 1997 · arXiv:cond-mat/9702168
Source status unknown — claims are unverified
Magnetic Phase Diagram of Ca2-xSrxRuO4 Governed by Structural Distortions
similarity 0.88Zhong Fang & Kiyoyuki Terakura · 2001 · arXiv:cond-mat/0103223
Source status unknown — claims are unverified
Electronic properties of the novel 4d metallic oxide SrRhO3
similarity 0.87K. Yamaura et al. · 2002 · arXiv:cond-mat/0208591
Source status unknown — claims are unverified