Soldering of MT-YBCO: method to produce superconductive junctions
T. Prikhna, W. Gawalek, N. Novikov, V. Moshchil, V. Sverdun, N. Sergienko, A. Surzhenko, M. Wendt, T. Habisreuther, D. Litzkendorf, S. Dub, R. Mueller, A. Kordyuk, S. Kracunovska, L. Alexandrova
arXiv:cond-mat/0204364 · 2002-04-17 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
A method of soldering of melt-textured YBa2Cu3O7-d -based (MT-YBCO) superconductive blocks using a TmBaCu3O7-d (Tm123) powder has been suggested. The method excludes stages of slow cooling during soldering and preparation of auxiliary layers. To estimate the critical current density (jc) through the obtained junction, we have drilled rings from single-domained MT-YBCO blocks, cut into two pieces along the diameters and soldered using a Tm123 powder. The critical current density, jc, (estimated using vibrating sample magnetometer) through the soldered ring was 34 kA/cm^2 in 0 T field at 77 K, which turned out to be even higher by a factor of approximately 1.5 than that through the single-domained material. The increase in jc through the soldered ring has been observed up to the 2.5 T field, while in the higher fields some decrease of jc took place. As a result of the field mapping of the trapped magnetic flux in soldered ring using a Hall probe, we obtained a regular truncated cone and the maximal level of trapped field for the ring 8 and 4 mm in outer and inner diameters was about 80 mT.
Similar papers
High field magneto-transport study of YBa2Cu3O7-Agx (x = 0.0 to 0.20)
similarity 0.86Poonam Rani et al. · 2013 · arXiv:1310.4628
Source status unknown — claims are unverified
Thermobaric Effect on Melt-Textured MBaCuO (M = Y, Nd)
similarity 0.85T. Prikhna et al. · 1999 · arXiv:cond-mat/9907054
Source status unknown — claims are unverified
Superconducting Bulk Magnets: Very High Trapped Fields and Cracking
similarity 0.85S. Gruss et al. · 2001 · arXiv:cond-mat/0104396
Source status unknown — claims are unverified
Superconducting joining of melt-textured Y-Ba-Cu-O bulk material
similarity 0.85T. Prikhna et al. · 2000 · arXiv:cond-mat/0007461
Source status unknown — claims are unverified
Superconductivity, intergrain, and intragrain critical current densities of materials
similarity 0.84J. R. Thompson et al.
Source status unknown — claims are unverified
Microwave absorption at low magnetic field in sintered YBa2Cu3O7: Freezing effects at low temperature and superconducting-glass model
similarity 0.84M. Giura et al.
Source status unknown — claims are unverified