The degradation of MgB2 under ambient environment
A. Serquis, Y. T. Zhu, D. E. Peterson, F. M. Mueller, R. K. Schulze, V. F. Nesterenko, S. S. Indrakanti
arXiv:cond-mat/0206492 · DOI 10.1063/1.1481548 · 2002-06-25 · Applied Physics Letters
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The superconductivities of samples prepared by several procedures were found to degrade under ambient environment. The degradation mechanism was studied by measuring the change of surface chemical composition of dense MgB2 pellets (prepared by hot isostatic pressure, HIPed) under atmospheric exposure using X-ray Photoelectron Spectroscopy (XPS). Results showed that samples with poor connectivity between grains and with smaller grain sizes degrade with time when exposed to ambient conditions. In these samples, the Tc did not change with time, but the superconducting transition became broader and the Meissner fraction decreased. In contrast, our well-sintered and the HIPed samples remained stable for several months under ambient condition. The degradation was found to be related to surface decomposition as observed by XPS. We observed the formation of oxidized Mg, primarily in the form of a Mg hydroxide, the increase of C and O contents, and the reduction of B concentration in the surface layer of MgB2 samples.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure unresolved | unknown |
Similar papers
Effects of proton irradiation and ageing on the superconducting properties of single crystalline and polycrystalline MgB2
similarity 0.86G. K. Perkins et al. · 2003 · arXiv:cond-mat/0305255
Source status unknown — claims are unverified
Influence of Mg Deficiency on the Superconductivity in MgB2 Thin Films Grown by using HPCVD
similarity 0.86Ji Young Huh et al. · 2007 · arXiv:0709.1989
Source status unknown — claims are unverified
Significant enhancement of irreversibility field in clean-limit bulk MgB2
similarity 0.85V. Braccini et al. · 2002 · arXiv:cond-mat/0208054
Source status unknown — claims are unverified
High-pressure high-temperature solution growth, structural, and superconducting properties of Fe-substituted MgB2 single crystals
similarity 0.85N. D. Zhigadlo & R. Puzniak · 2025 · arXiv:2505.16432
Source status unknown — claims are unverified
Roles of Fe-ion irradiation on MgB thin films: Structural, superconducting, and optical properties
similarity 0.85Dzung T. Tran et al. · 2025 · arXiv:2509.19697
Source status unknown — claims are unverified
Dependence of the flux creep activation energy on current density and magnetic field for MgB2 superconductor
similarity 0.85M. J. Qin et al. · 2001 · arXiv:cond-mat/0104112
Source status unknown — claims are unverified