Magnetic shielding in MgB2/Fe superconducting wires
J. Horvat, S. Soltanian, X. L. Wang, S. X. Dou
arXiv:cond-mat/0207727 · DOI 10.1109/TASC.2003.812303 · 2002-07-31 · IEEE Transactions on Applied Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Transport critical current (Ic) was measured for MgB2/Fe round wires, with magnetic field oriented perpendicular to the wire and parallel to it. Measurements were made on a wire with pure MgB2 core and another wire where MgB2 core was doped with nano-size SiC. This doping strongly improved the vortex pinning in MgB2. The field dependence of Ic was strongly improved due to the presence of the iron sheath. At 30K, Ic did not depend on the field for fields between 0.09 and 0.7T. At lower temperatures, Ic increased with the field, after initial decrease, resembling a "peak effect". This effect was extended to higher fields as the temperature went down: at 10K the peak appeared at 3.5T. This improvement was not due to mere magnetic shielding by iron, but more likely to an interaction between the iron sheath and superconductor. Improvement of vortex pinning did not affect the range of fields within which this effect was observed.
Similar papers
Improvement of critical current in MgB2/Fe wires by a ferromagnetic sheath
similarity 0.94J. Horvat et al. · 2001 · arXiv:cond-mat/0109283
Source status unknown — claims are unverified
Interaction of superconductor with magnetic sheath as a way for improvement of critical current in MgB2/Fe superconductor
similarity 0.93J. Horvat · 2003 · arXiv:cond-mat/0306083
Source status unknown — claims are unverified
Interaction between superconductor and ferromagnetic domains in iron sheath: peak effect in MgB2/Fe wires
similarity 0.93J. Horvat et al. · 2005 · arXiv:cond-mat/0507510
Source status unknown — claims are unverified
Doping Effect and Flux Pinning Mechanism of Nano-SiC Additions in MgB2 Strands
similarity 0.90Z. X. Shi et al. · 2011 · arXiv:1102.5573
Source status unknown — claims are unverified
Superconductivity of bulk MgB2 + nano(n)-SiC composite system: A high field magnetization study
similarity 0.88Arpita Vajpayee et al. · 2008 · arXiv:0802.3971
Source status unknown — claims are unverified
Properties of superconducting MgB_2 wires: "in-situ" versus "ex-situ" reaction technique
similarity 0.88Alexey V Pan et al. · 2003 · arXiv:cond-mat/0302249
Source status unknown — claims are unverified