High-pressure synthesis of superconducting Nb{1-x}B2 (x = 0-0.48) with the maximum Tc = 9.2 K
A. Yamamoto, C. Takao, T. Masui, M. Izumi, S. Tajima
arXiv:cond-mat/0208331 · DOI 10.1016/S0921-4534(02)01996-2 · 2002-08-16 · Physica C-superconductivity and Its Applications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Superconductivity with Tc above 9 K was found in metal-deficient NbB2 prepared under 5 GPa, while no clear superconductivity was observed down to 3 K in stoichiometric NbB2. The superconductivity was observed above x = 0.04 in Nb1-xB2. and the lattice parameters also changed abruptly at x = 0.04. As x increased, the transition temperature Tc slightly rose and fell with the maximum value of 9.2 K at x = 0.24 for the samples sintered at 5 GPa and 1200 C. The Tc-value changed in the range from 7 K to 9 K, depending on the sintering pressure. A series of Ta1-xB2 (0 =< x =< 0.24) was also synthesized under high pressure to examine a special effect of high-pressure synthesis.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Nb0.76B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9.2 | 5 GPa | unknown |
Similar papers
Theoretical Study of Electronic Structure and Superconductivity in Nb_(1-x)B_2 Alloys
similarity 0.93P. Jiji Thomas Joseph & Prabhakar P. Singh · 2003 · arXiv:cond-mat/0304437
Source status unknown — claims are unverified
Pressure dependence of the superconducting transition temperature in single-crystal NbBx (x near 2) with Tc=9.4 K
similarity 0.90J. E. Schirber et al.
Source status unknown — claims are unverified
Evidence of unconventional superconductivity in the Ni-doped NbB2 system
similarity 0.88S. T. Renosto et al. · 2018 · arXiv:1810.09976
Source status unknown — claims are unverified
High critical field superconductivity at ambient pressure in MoB2 stabilized in the P6/mmm structure via Nb substitution
similarity 0.87A. C. Hire et al.
Source status unknown — claims are unverified
Chemical pressure effect on Tc in BiS2-based Ce1-xNdxO0.5F0.5BiS2
similarity 0.87Joe Kajitani et al. · 2013 · arXiv:1311.4272
Source status unknown — claims are unverified
Discovery of superconductivity in technetium-borides at moderate pressures
similarity 0.87Xiangru Tao et al. · 2024 · arXiv:2403.15283
Source status unknown — claims are unverified