Reversible melting and equilibrium phase formation of (Bi,Pb)2Sr2Ca2Cu3O10+d
E. Giannini, I. Savysyuk, V. Garnier, R. Passerini, P. Toulemonde, R. Fluekiger
arXiv:cond-mat/0208459 · DOI 10.1088/0953-2048/15/11/316 · 2002-08-23
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The decomposition and the reformation of the (Bi,Pb)2Sr2Ca2Cu3O10+d (?Bi,Pb(2223)?) phase have been investigated in-situ by means of High-Temperature Neutron Diffraction, both in sintered bulk samples and in Ag-sheathed monofilamentary tapes. Several decomposition experiments were performed at various temperatures and under various annealing atmospheres, under flowing gas as well as in sealed tubes, in order to study the appropriate conditions for Bi,Pb(2223) formation from the melt. The Bi,Pb(2223) phase was found to melt incongruently into (Ca,Sr)2CuO3, (Sr,Ca)14Cu24O41 and a Pb,Bi-rich liquid phase. Phase reformation after melting was successfully obtained both in bulk samples and Ag-sheathed tapes. The possibility of crystallising the Bi,Pb(2223) phase from the melt was found to be extremely sensitive to the temperature and strongly dependent on the Pb losses. The study of the mass losses due to Pb evaporation was complemented by thermogravimetric analysis which proved that Pb losses are responsible for moving away from equilibrium and therefore hinder the reformation of the Bi,Pb(2223) phase from the melt. Thanks to the full pattern profile refinement, a quantitative phase analysis was carried out as a function of time and temperature and the role of the secondary phases was investigated. Lattice distortions and/or transitions were found to occur at high temperature in Bi,Pb(2223), Bi,Pb(2212), (Ca,Sr)2CuO3 and (Sr,Ca)14Cu24O41, due to cation diffusion and stoichiometry changes. The results indicate that it is possible to form the Bi,Pb(2223) phase from a liquid close to equilibrium conditions, like Bi(2212) and Bi(2201), and open new unexplored perspectives for high-quality Ag-sheathed Bi,Pb(2223) tape processing.
Similar papers
Evidence for superconductivity at 190 K in a pressure-overdoped cuprate
similarity 0.83Alexander C. Mark et al. · 2026 · arXiv:2608.00942
Source status unknown — claims are unverified
In-situ high energy synchrotron X-ray diffraction investigation of the MgB2 phase formation and MgB2 tapes sintering
similarity 0.81Maurizio Vignolo et al. · 2014 · arXiv:1405.4134
Source status unknown — claims are unverified
Signature of T above 111 K in Li-doped (Bi,Pb)-2223 superconductors: synergistic nature of hole concentration, coherence length and Josephson interlayer coupling
similarity 0.81N. K. Man & Huu T. Do · 2024 · arXiv:2405.04689
Source status unknown — claims are unverified
Enhanced Superconductivity in Close Proximity to the Structural Phase Transition of Sr1-xBaxNi2P2
similarity 0.80Kazutaka Kudo et al. · 2017 · arXiv:1702.02677
Source status unknown — claims are unverified
Low-Temperature Phase Transition in Bi_2Sr_2Ca(Ni_xCu_{1-x})_20_8: Evidence for Unconventional Superconductivity
similarity 0.80R. Movshovich et al. · 1997 · arXiv:cond-mat/9709061
Source status unknown — claims are unverified
Magnetic flux jumps in textured Bi2Sr2CaCu2O(8+d)
similarity 0.80A. Nabialek et al. · 2002 · arXiv:cond-mat/0209430
Source status unknown — claims are unverified