Superconductivity of up to 80 K for Tb-123 - TbSr2Cu2.7Mo0.3O7
V. P. S. Awana, H. Kishan, E. Takayama-Muromachi, T. Watanabe, M. Karppinen, H. Yamauchi, S. K. Malik, W. B. Yelon, V. Ganesan, A. V. Narlikar
arXiv:cond-mat/0305555 · 2003-05-23 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The Tb-123 phase has been synthesized in single-phase form with the composition TbSr2Cu2.7Mo0.3O7 by solid-state reaction route and its phase purity is confirmed by neutron powder diffraction experiments. As-synthesized sample does not show superconductivity down to 5 K. An unusually high antiferromagnetic ordering temperature (TN) of around 7 K is seen for Tb. After 120-atm-O2 post-annealing, bulk superconductivity is achieved in the compound at around 30 K, without any significant effect on TN. To achieve higher oxygen content and higher Tc, the as-synthesized sample is subjected to high-pressure oxygenation (HPO) carried out in a closed cell at 5 GPa and 400 oC in the presence of AgO as an excess-oxygen source. This sample exhibited superconductivity onset at around 80 K with a Meissner fraction of larger than 10 % at 5 K. Our observation of superconductivity at 80 K is the highest Tc to-date among the Tb-123 compounds.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| TbSr2Cu2.7Mo0.3O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 30 | Pressure not reported | unknown |
| TbSr2Cu2.7Mo0.3O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 80 | 5 GPa | onset |
Similar papers
Preparation and properties of superconducting Y(Ba1−xSrx)2Cu4O8
similarity 0.87Takahiro Wada et al.
Source status unknown — claims are unverified
Overdoped Cuprates With High Temperature Superconducting Transitions
similarity 0.86M. Marezio et al. · 2012 · arXiv:1207.4239
Source status unknown — claims are unverified
Eight rare-earth-substituted Pb-based 1:2:1:2 superconducting compounds: (Pb,Cu)Sr2(Ca,R)Cu2O7 (R=Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm)
similarity 0.85H. B. Liu & D. E. Morris
Source status unknown — claims are unverified
Observation of high-Tc superconductivity in inhomogeneous combinatorial ceramics
similarity 0.85Mitra Iranmanesh et al. · 2018 · arXiv:1812.06273
Source status unknown — claims are unverified
Superconductivity up to 114 K in the Bi-Al-Ca-Sr-Cu-O compound system without rare-earth elements
similarity 0.85C. W. Chu et al.
Source status unknown — claims are unverified
Synthesis and characterization of the superconducting cuprates (Pb,Cu)Sr2(Y,Ca)Cu2Oz
similarity 0.84Toshihiko Maeda et al.
Source status unknown — claims are unverified