Effect of Sr substitution on the stability of CuO chains in oxygen and nitrogen annealed YBa2-xSrxCu3O(x = 0.0, 0.50, 1.0) superconducting system
M. A. Ansari, V. P. S. Awana, Anurag Gupta, R. B. Saxena, H. Kishan
arXiv:cond-mat/0311564 · 2003-11-25 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Samples of YBa2-xSrxCu3O7-d (x = 0.0, 0.50, 1.0) series were synthesized by solid-state reaction and first annealed in flowing O2 gas. All samples crystallized in orthorhombic structure, where orthorhombic distortion was found to decrease with an increase in x. Four probe resistivity measurements showed that superconducting transition temperature (Tc) decreases monotonically with x at a rate of dTc/dx = 1.3 K/at%. The sample with x=0 had a Tc = 91 K. The samples were further annealed in flowing N2 gas at 450 0C. The Tc of all samples decreased by nitrogen annealing. Interestingly, the decrease in Tc(x) became nearly three times larger at a rate of dTc/dx = 3.7 K/at%. The sample with x=0 had a Tc = 42 K. We discuss possible reasons and implications of the Tc(x) suppression vis stability of CuO chains. Key words: Y-123, Sr substitution, Superconducting transition
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| YBa2Cu3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 91 | Pressure not reported | unknown |
| YBa2Cu3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 42 | Pressure not reported | unknown |
Similar papers
Relationship between superconductivity and crystalline stability of the Y-Ba-Cu-O system
similarity 0.90H. Zhang et al.
Source status unknown — claims are unverified
Superconductivity and microstructure of YSr2Cu3O6.875
similarity 0.89O. I. Lebedev et al.
Source status unknown — claims are unverified
Effect of oxygen deficiency on the normal and superconducting properties of YBa2Cu3O7−δ
similarity 0.89S. I. Park et al.
Source status unknown — claims are unverified
Systematic induction of superconductivity in Y1-xCaxBa2Cu3O6.3 system
similarity 0.89V. P. S. Awana et al. · 2004 · arXiv:cond-mat/0403230
Source status unknown — claims are unverified
Ca-substitution and O-doping effects in superconducting Cu(Ba0.8Sr0.2)2(Yb1−xCax)Cu2O6+z obtained from neutron diffraction refinements
similarity 0.89M. Karppinen et al.
Source status unknown — claims are unverified
Role of bond lengths in the 90-K superconductor: A neutron powder-diffraction study of YBa2Cu3−xCoxO7−y
similarity 0.89P. F. Miceli et al.
Source status unknown — claims are unverified