Study of the SmBaCuO solid solutions decomposition and its possible role for changing critical current
N. I. Matskevich, A. I. Romanenko, L. V. Yakovkina, Th. Wolf, G. Krabbes
arXiv:cond-mat/0401277 · 2004-01-16 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We studied thermochemical characteristics of the Sm1+xBa2-xCu3Oy single crystals by solution calorimetry. Dependences of formation enthalpies from samarium content were constructed. It was established that solid solutions on the bases of Sm123 could be decomposed both in inert and in oxygen atmosphere into different mixtures. We supposed that solid solutions decomposition could lead to increasing critical current density. We assumed from thermochemical data that Jc could be greater for samples prepared in oxygen than for samples synthesized in inert atmosphere. We confirmed these assumptions by comparison of obtained thermochemical data with transport properties measured in literature. We also investigated temperature dependences of resistance in the temperature range of 300-550 K during slow heating. As it was shown there was anomaly of resistance near 500 K. The origin of this anomaly was discussed.
Similar papers
Effect of compositional variation and annealing in oxygen on superconducting properties of Y1Ba2Cu3O8−y
similarity 0.83A. J. Panson et al.
Source status unknown — claims are unverified
Superconductivity above 90 K in the square-planar compound system ABa2Cu3O6+x with A=Y, La, Nd, Sm, Eu, Gd, Ho, Er and Lu
similarity 0.82P. H. Hor et al.
Source status unknown — claims are unverified
Evidence for possible stable superconductivity at 500 K
similarity 0.82A. Erbil et al.
Source status unknown — claims are unverified
High-Tc superconductivity in regions of possible compound formation: Y2−xBaxCuO4−x/2+δ and Y2−xBa1+xCu2O6−x/2+δ
similarity 0.82Shiou-Jyh Hwu et al.
Source status unknown — claims are unverified
Superconductivity above 90 K in the compound YBa2Cu3Ox: Structural, transport, and magnetic properties
similarity 0.81P. M. Grant et al.
Source status unknown — claims are unverified
Superconductivity in single-phase Y1Ba2Cu3O9−x and thermoelectric power measurement
similarity 0.80Z. G. Khim et al.
Source status unknown — claims are unverified