Magnetism and superconductivity in $M_{c}$Ta$_{2}$S$_{2}$C (M = Fe, Co, Ni, and Cu)

Masatsugu Suzuki; Itsuko S. Suzuki; Jürgen Walter

doi:10.1103/PhysRevB.71.224407

← Back to search

Magnetism and superconductivity in $M_{c}$Ta$_{2}$S$_{2}$C (M = Fe, Co, Ni, and Cu)

Masatsugu Suzuki, Itsuko S. Suzuki, Jürgen Walter

arXiv:cond-mat/0402501 · DOI 10.1103/PhysRevB.71.224407 · 2004-02-19 · Physical Review B

T2theoretical5 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Magnetic properties of $M_{c}$Ta$_{2}$S$_{2}$C ($M$ = Fe, Co, Ni, Cu) have been studied using SQUID DC and AC magnetic susceptibility. In these systems magnetic $M^{2+}$ ions are intercalated into van der Waals gaps between adjacent S layers of host superconductor Ta$_{2}$S$_{2}$C. Fe$_{0.33}$Ta$_{2}$S$_{2}$C is a quasi 2D $XY$-like antiferromagnet on the triangular lattice. It undergoes an antiferromagnetic phase transition at $T_{N}$ (= 117 K). The irreversible effect of magnetization occurs below $T_{N}$, reflecting the frustrated nature of the system. The AF phase coexists with two superconducting phases with the transition temperatures $T_{cu} = 8.8$ K and $T_{cl} = 4.6$ K. Co$_{0.33}$Ta$_{2}$S$_{2}$C is a quasi 2D Ising-like antiferromagnet on the triangular lattice. The antiferromagnetic phase below $T_{N} = 18.6$ K coexists with a superconducting phase below $T_{cu} = 9.1$ K. Both Ni$_{0.25}$Ta$_{2}$S$_{2}$C and Cu$_{0.60}$Ta$_{2}$S$_{2}$C are superconductors with $T_{cu}$ ($= 8.7$ K for Ni and 6.4 K for Cu) and $T_{cl}$ (= 4.6 K common to $M_{c}$Ta$_{2}$S$_{2}$C). Very small effective magnetic moments suggest that Ni$^{2+}$ and Cu$^{2+}$ spins are partially delocalized.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Fe0.33Ta2S2C Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.8	Pressure not reported	unknown
Fe0.33Ta2S2C Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.6	Pressure not reported	unknown
Co0.33Ta2S2C Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9.1	Pressure not reported	unknown
Co0.33Ta2S2C Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.6	Pressure not reported	unknown
Ni0.25Ta2S2C Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.7	Pressure not reported	unknown
Ni0.25Ta2S2C Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.6	Pressure not reported	unknown
Cu0.60Ta2S2C Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	6.4	Pressure not reported	unknown
Cu0.60Ta2S2C Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.6	Pressure not reported	unknown
Ta2S2C Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	3.61	Pressure not reported	unknown
Ta2S2C Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.9	Pressure not reported	unknown