V. P. S. Awana, M. A. Ansari, Anurag Gupta, R. B. Saxena, H. Kishan, Devendra Buddhikot, S. K. Malik
arXiv:cond-mat/0403229 · 2004-03-09 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The RuSr2Gd1.5Ce0.5Cu2O10-d (Ru-1222) compounds, with varying oxygen content, crystallize in a tetragonal crystal structure (space group I4/mmm). Resistance (R) versus temperature (T) measurements show that the air-annealed samples exhibit superconductivity with superconducting transition temperature (Tc) onset at around 32 K and R=0 at 3.5 K. On the other hand, the N2-annealed sample is semiconducting down to 2 K. Magneto-transport measurements on air-annealed sample in applied magnetic fields of 3 and 6 Tesla show a decrease in both Tc onset and TR=0. Magnetoresistance of up to 20% is observed in N2-annealed sample at 2 K and 3 T applied field. The DC magnetization data (M vs. T) reveal magnetic transitions (Tmag.) at 100 K and 106 K, respectively, for both air- and N2-annealed samples. Ferromagnetic components in the magnetization are observed for both samples at 5K and 20 K. The superconducting transition temperature (Tc) seems to compete with the magnetic transition temperature (Tmag.). Our results suggest that the magnetic ordering temperature (Tmag.) of Ru moments in RuO6 octahedra may have direct influence/connection with the appearance of superconductivity in Cu-O2 planes of Ru-1222 compounds. Key words: Ruthenocuprates, Superconductivity and Magnetism, Magneto transport and Magneto resistance. PACS: 74.25. Ha, 74.72. Jt, 75.25. +z, 75.30. Cr.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| RuSr2Gd1.5Ce0.5Cu2O10-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 32 | Pressure not reported | onset |
| RuSr2Gd1.5Ce0.5Cu2O10-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 3.5 | Pressure not reported | zero_resistance |
Similar papers
Possible competition between superconductivity and magnetism in RuSr2Gd1.5Ce0.5Cu2O10−δ ruthenocuprate compounds
similarity 0.99V. P. S. Awana et al.
Source status unknown — claims are unverified
The characteristics of the superconducting and magnetic phases in the polycrystalline samples of ruthenocuprates of nominal compositions RuSr2GdCu2O8, Ru0.98Sr2GdCu2O8 and Ru0.5Sr2GdCu2.5O8-d
similarity 0.93Piotr W. Klamut et al. · 2009 · arXiv:0905.1721
Source status unknown — claims are unverified
Direct Observation of Coexistence of Ferromagnetism and Superconductivity in RuSr2(Gd0.7Ce0.3)2Cu2O10
similarity 0.92S. Y. Chen et al. · 2001 · arXiv:cond-mat/0105510
Source status unknown — claims are unverified
Hysteresis and stepwise structure in MR curves of granular superconducting ruthenocuprates RuSr(GdCeCuO}
similarity 0.92B. I. Belevtsev et al. · 2012 · arXiv:1205.6743
Source status unknown — claims are unverified
Transport, thermal and magnetic properties of RuSr_2(Gd_{1.5}Ce_{0.5})Cu_2O_{10-δ}, a magnetic superconductor
similarity 0.90D. G. Naugle et al. · 2005 · arXiv:cond-mat/0511489
Source status unknown — claims are unverified
Ruthenocuprates RuSr2(Eu,Ce)2Cu2O10: Intrinsic magnetic multilayers
similarity 0.90I. Zivkovic et al. · 2001 · arXiv:cond-mat/0110181
Source status unknown — claims are unverified