Al substitution in MgB2 crystals: influence on superconducting and structural properties
J. Karpinski, N. D. Zhigadlo, G. Schuck, S. M. Kazakov, B. Batlogg, K. Rogacki, R. Puzniak, J. Jun, E. Muller, P. Wagli, R. Gonnelli, D. Daghero, G. A. Ummarino, V. A. Stepanov
arXiv:cond-mat/0411449 · DOI 10.1103/PhysRevB.71.174506 · 2004-11-17 · Physical Review B
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Single crystals of Mg1-xAlxB2 have been grown at a pressure of 30 kbar using the cubic anvil technique. Precipitation free crystals with x < 0.1 were obtained as a result of optimization of already developed MgB2 crystal growth procedure. Systematic decrease of the c-axis lattice constant with increasing Al content, when the a-axis lattice constant is practically unchanged, was observed. Variation of the critical temperature on Al content in Mg1-xAlxB2 crystals was found to be slightly different than that one observed for polycrystalline samples since, even a very small substitution of 1-2% of Al leads to the decrease of Tc by about 2-3 K. X-ray and high resolution transmission electron microscopy investigations indicate on the appearance of second precipitation phase in the crystals with x > 0.1. This is in a form of non-superconducting MgAlB4 domains in the structure of superconducting Mg1-xAlxB2 matrix. Resistivity and magnetic investigations show the slight increase of the upper critical field, Hc2, for H//c for the samples with small x, significant reduction of the Hc2 anisotropy at lower temperatures, and decrease of the residual resistance ratio value for Al substituted samples as compared to those of unsubstituted crystals. Superconducting gaps variation as a function of Al content, investigated with point contact spectroscopy for the series of the crystals with Tc in the range from 20 to 37 K, does not indicate on the merging of the gaps with decreasing Tc down to 20 K. It may be related to an appearance of the precipitation phase in the Mg1-xAlxB2 structure.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Mg1-xAlxB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 20 | Pressure not reported | unknown |
| Mg1-xAlxB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 37 | Pressure not reported | unknown |
Similar papers
Al substitution in MgB2 crystals: Influence on superconducting and structural properties
similarity 1.00J. Karpinski et al.
Source status unknown — claims are unverified
Aluminium substitution induced superstructures in Mg1-xAlxB2 (x = 0.0 to 0.50): An X-ray diffraction study
similarity 0.92Monika Mudgel et al. · 2007 · arXiv:0708.3882
Source status unknown — claims are unverified
Superconducting properties and c-axis superstructure of Mg1−xAlxB2
similarity 0.91J. Y. Xiang et al.
Source status unknown — claims are unverified
Ab initio modeling of superconducting alloys
similarity 0.90Pedro N. Ferreira et al. · 2024 · arXiv:2406.15174
Source status unknown — claims are unverified
Structural and Superconducting Transitions in Mg_{1-x}Al_{x}B_2
similarity 0.89Sergey V. Barabash & David Stroud · 2001 · arXiv:cond-mat/0111392
Source status unknown — claims are unverified
Crystal structure of the MgAlB superconductors near x=0.5
similarity 0.89S. Margadonna et al. · 2002 · arXiv:cond-mat/0204015
Source status unknown — claims are unverified