Resistivity and Thermoelectric power of NaxCoO2 (x =1.0, 0.7 and 0.6) system
H. Kishan, V. P. S. Awana, M. A. Ansari, Anurag Gupta, R. B. Saxena, V. Ganesan, A. V. Narlikar, C. A. Cardoso, R. Nirmala, Devendra Buddhikot, S. K. Malik
arXiv:cond-mat/0412122 · DOI 10.1063/1.1847852 · 2004-12-06 · Journal of Applied Physics
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Results of thermo-electric power (S) and electrical resistivity (r) measurements are reported on NaxCoO2 compounds with x = 1.0, 0.7 and 0.6. These are single-phase compounds crystallizing in the hexagonal structure (space group P63/mmc) at room temperature. Thermo-electric power values at 300K (S300K) are, 80mV/K, 39mV/K and 37mV/K for x = 1.0, 0.7 and 0.6 samples, respectively. The samples with x=0.7 and 1.0 are metallic down to 5 K, while the x = 0.6 sample is semiconducting. The value of r300K for x = 1.0 sample is \~0.895 mW-cm and the power factor (S2/r) is = 7.04 x 10-3 W/mK2 which qualifies it as a good thermo-electric material. In x =1.0 sample, S(T) is positive throughout 300-5K temperature range and decreases monotonically to zero as temperature T= 0. In contrast, S(T) of x = 0.7 and 0.6 samples changes sign and shows negative values between 90 K and 16 K before approaching zero as T = 0. Anomalous S(T) behavior of x = 0.6 and 0.7 samples, which are coincidentally the precursor materials to the reported superconductivity in this class of materials, indicates a dramatic change in the electronic structure of these compounds on lowering the Na content.
Similar papers
Superconductivity, charge ordering and structural properties of alpha and beta-NaxCoO2.y(H2O, D2O)
similarity 0.89Y. G. Shi et al. · 2005 · arXiv:cond-mat/0508502
Source status unknown — claims are unverified
The crystal growth and characterization of NaxCoO2 and NaxCoO2yH2O
similarity 0.86D. P. Chen et al. · 2004 · arXiv:cond-mat/0401636
Source status unknown — claims are unverified
Superconductivity Phase Diagram of Na(x)CoO(2).1.3H(2)O
similarity 0.86R. E. Schaak et al. · 2003 · arXiv:cond-mat/0305450
Source status unknown — claims are unverified
Fermi surface and quasiparticle dynamics of Na(x)CoO2 {x=0.7} investigated by Angle-Resolved Photoemission Spectroscopy
similarity 0.85M. Z. Hasan et al. · 2003 · arXiv:cond-mat/0308438
Source status unknown — claims are unverified
Superconductivity in epitaxial thin films of NaxCoO2 y D2O
similarity 0.85Y. Krockenberger et al. · 2007 · arXiv:0705.0517
Source status unknown — claims are unverified
The role of doping and dimensionality in the superconductivity of NaxCoO2
similarity 0.85M. Banobre-Lopez et al. · 2004 · arXiv:cond-mat/0409606
Source status unknown — claims are unverified