Impact of Zn substitution on phase formation and superconductivity of Bi1.6Pb0.4 Sr2Ca2Cu3-xZnxO10 with x = 0.0, 0.015, 0.03, 0.06, 0.09 and 0.12
R. B. Saxena, Rajiv Giri, V. P. S. Awana, H. K. Singh, M. A. Ansari, B. V. Kumaraswamy, Anurag Gupta, Rashmi Nigam1, K. P. Singh, H. Kishan, O. N. Srivastava
arXiv:cond-mat/0505461 · DOI 10.1142/S0217984905008785 · 2005-05-19 · Modern Physics Letters B
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Samples of series Bi1.6Pb0.4Sr2Ca2Cu3-xZnxO10 with x = 0.0, 0.015, 0.03, 0.06, 0.09 and 0.12 are synthesized by solid-state reaction route. All the samples crystallize in tetragonal structure with majority (> 90%) of Bi-2223 (Bi2Sr2Ca2Cu3O10) phase (c-lattice parameter ~ 36 A0). The proportion of Bi-2223 phase decreases slightly with an increase in x. The lattice parameters a and c of main phase (Bi-2223) do not change significantly with increasing x. Superconducting critical transition temperature (Tc) decreases with x as evidenced by both resistivity [(T)] and AC magnetic susceptibility [(T)] measurements. Interestingly the decrement of Tc is not monotonic and the same saturates at around 96 K for x > 0.06. In fact Tc decreases fast (~10K/at%) for x = 0.015 and 0.03 samples and later nearly saturates for higher x values. Present results of Zn doping in Bi-2223 system are compared with Zn doped other HTSC (High temperature superconducting) systems, namely the RE-123 (REBa2Cu3O7) and La-214 ((La,Sr)2CuO4).
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Bi1.6Pb0.4Sr2Ca2Cu3O10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
| Bi1.6Pb0.4Sr2Ca2Cu3O10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
| Bi1.6Pb0.4Sr2Ca2Cu2.985Zn0.015O10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
| Bi1.6Pb0.4Sr2Ca2Cu2.985Zn0.015O10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
| Bi1.6Pb0.4Sr2Ca2Cu2.97Zn0.03O10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
| Bi1.6Pb0.4Sr2Ca2Cu2.97Zn0.03O10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
| Bi1.6Pb0.4Sr2Ca2Cu2.94Zn0.06O10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 96 | Pressure not reported | unknown |
| Bi1.6Pb0.4Sr2Ca2Cu2.94Zn0.06O10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 96 | Pressure not reported | unknown |
| Bi1.6Pb0.4Sr2Ca2Cu2.91Zn0.09O10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 96 | Pressure not reported | unknown |
| Bi1.6Pb0.4Sr2Ca2Cu2.91Zn0.09O10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 96 | Pressure not reported | unknown |
| Bi1.6Pb0.4Sr2Ca2Cu2.88Zn0.12O10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 96 | Pressure not reported | unknown |
| Bi1.6Pb0.4Sr2Ca2Cu2.88Zn0.12O10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 96 | Pressure not reported | unknown |
Similar papers
Diamagnetism above Tc in underdoped Bi2.2Sr1.8Ca2Cu3O10+d
similarity 0.90Tetsuya Iye et al. · 2010 · arXiv:1008.4327
Source status unknown — claims are unverified
Unusual T_c variation with hole concentration in Bi_2Sr_{2-x}La_xCuO_{6+δ}
similarity 0.89Mu-Yong Choi & J. S. Kim · 2000 · arXiv:cond-mat/0001339
Source status unknown — claims are unverified
Growth and Characterization of BiSrCuO Single Crystals
similarity 0.88Huiqian Luo et al. · 2006 · arXiv:cond-mat/0611349
Source status unknown — claims are unverified
Stability of superconducting phases in Bi-Sr-Ca-Cu-O and the role of Pb doping
similarity 0.88S. X. Dou et al.
Source status unknown — claims are unverified
Doping Dependencies of Onset Temperatures for the Pseudogap and Superconductive Fluctuation in BiSrCaCuO, Studied from both In-Plane and Out-of-Plane Magnetoresistance Measurements
similarity 0.88Tomohiro Usui et al. · 2014 · arXiv:1404.4736
Source status unknown — claims are unverified
Effect of lead substitution in bismuth-based cuprate systems containing both low-Tc and high-Tc phases
similarity 0.88A. K. Bandyopadhyay et al.
Source status unknown — claims are unverified