Effects of Neutron Irradiation on Carbon Doped MgB2 Wire Segments

R. H. T. Wilke; S. L. Bud'ko; P. C. Canfield; D. K. Finnemore; Raymond J. Suplinskas; J. Farmer; S. T. Hannahs

doi:10.1088/0953-2048/19/6/024

← Back to search

Effects of Neutron Irradiation on Carbon Doped MgB2 Wire Segments

R. H. T. Wilke, S. L. Bud'ko, P. C. Canfield, D. K. Finnemore, Raymond J. Suplinskas, J. Farmer, S. T. Hannahs

arXiv:cond-mat/0507275 · DOI 10.1088/0953-2048/19/6/024 · 2005-07-12 · Superconductor Science and Technology

T2theoretical10 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We have studied the evolution of superconducting and normal state properties of neutron irradiated Mg(B$_{.962}$C$_{.038}$)$_2$ wire segments as a function of post exposure annealing time and temperature. The initial fluence fully suppressed superconductivity and resulted in an anisotropic expansion of the unit cell. Superconductivity was restored by post-exposure annealing. The upper critical field, H$_{c2}$(T=0), approximately scales with T$_c$ starting with an undamaged T$_c$ near 37 K and H$_{c2}$(T=0) near 32 T. Up to an annealing temperature of 400 $^ o$C the recovery of T$_c$ tends to coincide with a decrease in the normal state resistivity and a systematic recovery of the lattice parameters. Above 400 $^ o$C a decrease in order along the c- direction coincides with an increase in resistivity, but no apparent change in the evolution of T$_c$ and H$_{c2}$. To first order, it appears that carbon doping and neutron damaging effect the superconducting properties of MgB$_2$ independently.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Mg(B.962C.038)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	37	Pressure not reported	unknown
Mg(B.962C.038)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	10	Pressure not reported	unknown
Mg(B.962C.038)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26	Pressure not reported	unknown
Mg(B.962C.038)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Mg(B.962C.038)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Mg(B.962C.038)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Mg(B.962C.038)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Mg(B.962C.038)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Mg(B.962C.038)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	10	Pressure not reported	unknown