Enhancement of the upper critical field of Nb3Sn utilizing disorder introduced by ball milling the elements
L. D. Cooley, Y. F. Hu, A. R Moodenbaugh
arXiv:cond-mat/0511560 · DOI 10.1063/1.2193047 · 2005-11-23
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Nb3Sn was prepared by milling Nb and Sn powder mixtures followed by limited reactions to restrict disorder recovery. Although disorder reduced the superconducting critical temperature Tc, the concomitant electron scattering increased the upper critical field mu0Hc2 to as high as 35 T at 0 K, as determined by the Werthamer-Helfand-Hohenberg equation. Hc2 was higher for longer milling times and lower annealing temperatures. Substitution of 2% Ti for Nb did not appreciably enhance Hc2, suggesting that alloying mitigates the benefits of disorder. Since alloyed Nb3Sn wires have mu0Hc2(0) approximately 29 T, wires based on heavily milled powders could extend the field range for applications if they can be made with high current density.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Nb3Sn Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
| Nb3Sn Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
Influence of Nb Alloying on Nb Recrystallization and the Upper Critical Field of Nb3Sn
similarity 0.91Nawaraj Paudel et al. · 2024 · arXiv:2412.09514
Source status unknown — claims are unverified
Evidence that the upper critical field of Nb3Sn is independent of whether it is cubic or tetragonal
similarity 0.90Jian Zhou et al. · 2011 · arXiv:1102.5118
Source status unknown — claims are unverified
Ternary Nb3Sn superconductors with artificial pinning centers and high upper critical fields
similarity 0.88Xingchen Xu et al. · 2018 · arXiv:1810.10569
Source status unknown — claims are unverified
Performance Boost in Industrial Multifilamentary Nb3Sn Wires due to Radiation Induced Pinning Centers
similarity 0.86T. Baumgartner et al. · 2015 · arXiv:1504.05366
Source status unknown — claims are unverified
Enhancement of the upper critical field in the cubic Laves-phase superconductor HfV by Nb doping
similarity 0.86Jifeng Wu et al. · 2019 · arXiv:1908.10007
Source status unknown — claims are unverified
Ta, Ti and Hf effects on NbSn high-field performance: temperature-dependent dopant occupancy and failure of Kramer extrapolation
similarity 0.85Chiara Tarantini et al. · 2019 · arXiv:1908.07548
Source status unknown — claims are unverified