V. P. S. Awana, M. Isobe, K. P. Singh, Md. Shahabuddin, H. Kishan, E. Takayama-Muromachi
arXiv:cond-mat/0601359 · DOI 10.1088/0953-2048/19/6/023 · 2006-01-17 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Polycrystalline MgB2 samples with 0, 2, 4 and 6 percent added nano-Co3O4 being synthesized by vacuum (10-5 Torr) annealing at 750 0C for three hours each are found to be nearly single phase with presence of only a small quantity of Mg/MgO in pristine sample and in addition the Co2O3 in doped compounds. All the samples exhibited clear and sharp diamagnetic transitions at around 38 K, in Zero-field-cooled (ZFC) magnetic susceptibility measurements with sizeable signal. The Field cooled (FC) measurements though having sharp transitions, but showed a very small signal, indicating high level of pinning centers in these samples. Further some of the doped samples exhibited Paramagnetic-Meissner-Effect (PME) in applied field of 5 Oe. The critical current density (Jc), being estimated by invoking Bean model for the pristine compound increase by nearly an order of magnitude for 2 and 4 percent nano-Co3O4 doping and later the same decreases sharply for 6 percent sample at nearly all studied temperatures and applied fields. Further the increased Jc (~ 10^8 A/cm2) is coupled with fluxiod jumps (T = 20 K and H = 1 T). Fluxiod Jumps are not seen in relatively low Jc pristine or 6 percent sample. This means the fluxiod-jumps are intrinsic only to the high Jc samples.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 38 | Pressure not reported | onset |
Similar papers
Effect of nano-carbon particle doping on the flux pinning properties of MgB2 superconductor
similarity 0.87S. Soltanian et al. · 2003 · arXiv:cond-mat/0302530
Source status unknown — claims are unverified
High Critical Current Density and Improved Irreversibility Field in Bulk MgB2 Made By A Scaleable, Nanoparticle Addition Route
similarity 0.86J. Wang et al. · 2002 · arXiv:cond-mat/0204472
Source status unknown — claims are unverified
Nanoscale-SiC doping for enhancing Jc and Hc2 in the Superconducting MgB2
similarity 0.86S. X. Dou et al. · 2003 · arXiv:cond-mat/0308265
Source status unknown — claims are unverified
Effect of nano-C doping on the in-situ processed MgB2 tapes
similarity 0.85Xianping Zhang et al. · 2005 · arXiv:cond-mat/0509475
Source status unknown — claims are unverified
Nanoscale grains, high irreversibility field, and large critical current density as a function of high energy ball milling time in C-doped magnesium diboride
similarity 0.85B. J. Senkowicz et al. · 2007 · arXiv:0712.2056
Source status unknown — claims are unverified
Dependence of the flux-creep activation energy on current density and magnetic field for the MgB2 superconductor
similarity 0.85M. J. Qin et al.
Source status unknown — claims are unverified