Coupling losses and transverse resistivity of multifilament YBCO coated superconductors
M. Polak, L. Krempasky, E. Usak, L. Jansak, E. Demencik, G. A. Levin, P. N. Barnes, D. Wehler, B. Moenter
arXiv:cond-mat/0602422 · DOI 10.1088/1742-6596/43/1/145 · 2006-02-17 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We studied the magnetization losses of four different types of filamentary YBCO coated conductors. A 10 mm wide YBCO coated conductor was subdivided into 20 filaments by laser cutting. The separation of coupling loss from the total is possible because the energy loss per cycle in samples with electrically insulated filaments has a very small frequency dependence. We measured the frequency dependence of the total losses in the frequency range between 0.1 Hz and 500 Hz. The coupling loss was obtained from the total by subtracting the hysteresis loss. The latter was measured at low frequencies since only hysteresis loss is non-negligible at frequencies below 1 Hz. The transverse resistivity was determined from the coupling losses; it was assumed that the sample length is equal to half of the twist pitch. The values of transverse resistivity deduced from the loss data were compared with those obtained by the four-point measurements with current flowing perpendicular to the filaments. Preliminary results indicate that the current method of laser ablation creates electrical contacts between the superconducting filaments and the substrate. This was also confirmed by the Hall probe mapping of the magnetic field in the vicinity of the tape. The measured transverse resistivity was close to the resistivity of the substrate (Hastelloy).
Similar papers
AC Losses of Copper Stabilized Multifilament YBCO Coated Conductors
similarity 0.93G. A. Levin et al. · 2012 · arXiv:1212.0452
Source status unknown — claims are unverified
AC-Tolerant Multifilament Coated Conductors
similarity 0.93G. A. Levin et al. · 2006 · arXiv:cond-mat/0609480
Source status unknown — claims are unverified
Multifilament YBa2Cu3O6+x -coated conductors with minimized coupling losses
similarity 0.91G. A. Levin et al. · 2006 · arXiv:cond-mat/0605313
Source status unknown — claims are unverified
Computation of Losses in HTS Under the Action of Varying Magnetic Fields and Currents
similarity 0.86Francesco Grilli et al. · 2013 · arXiv:1306.6251
Source status unknown — claims are unverified
The Integration of YBCO Coated Conductors into Magnets and Rotating Machinery
similarity 0.86G. A. Levin & P. N. Barnes · 2005 · arXiv:cond-mat/0509347
Source status unknown — claims are unverified
Numerical evaluation of AC losses in an HTS insert coil for high field magnet during its energization
similarity 0.86K. Kajikawa et al. · 2014 · arXiv:1405.7765
Source status unknown — claims are unverified