The doping effect of multiwall carbon nanotube on MgB2/Fe superconductor wire
J. H. Kim, W. K. Yeoh, M. J. Qin, X. Xu, S. X. Dou
arXiv:cond-mat/0603566 · DOI 10.1063/1.2209188 · 2006-03-22 · Journal of Applied Physics
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We evaluated the doping effect of two types of multiwall carbon nanotube (CNT) with different aspect ratios on MgB2/Fe monofilament wires. Relationships between microstructure, magnetic critical current density (Jc), critical temperature (Tc), upper critical field (Hc2), and irreversibility field (Hirr) for pure and CNT doped wires were systematically studied for sintering temperature from 650oC to 1000oC. As the sintering temperature increased, Tc for short CNT doped sample slightly decreased, while Tc for long CNT doped sample increased. This indicates better reactivity between MgB2 and short CNT due to its small aspect ratio and substitution of carbon (C) from short CNT for boron (B) occurs. In addition, short CNT doped samples sintered at the high temperatures of 900oC and 1000oC exhibited excellent Jc, and that value was approximately 104 A/cm2 in fields up to 8 T at 5 K. This suggests that short CNT is a promising carbon source for MgB2 superconductor with excellent Jc. In particular, inclusion of nanosized MgO particles and substitution of C into the MgB2 lattice could result in strong flux pinning centers.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Effect of carbon nanotube doping on critical current density of MgB2 superconductor
similarity 0.95S. X. Dou et al. · 2003 · arXiv:cond-mat/0310196
Source status unknown — claims are unverified
Enhancement of in-field Jc in MgB2/Fe wire using single and multi-walled nanotubes
similarity 0.93J. H. Kim et al. · 2006 · arXiv:cond-mat/0607540
Source status unknown — claims are unverified
Improved Critical Current Density of MgB2 Carbon Nanotubes (CNTs) Composite
similarity 0.93Chandra Shekhar et al. · 2006 · arXiv:cond-mat/0608700
Source status unknown — claims are unverified
Correlated enhancement of Hc2 and Jc in carbon nanotube-doped MgB2
similarity 0.92A. Serquis et al. · 2006 · arXiv:cond-mat/0612403
Source status unknown — claims are unverified
Alignment of Carbon Nanotube Additives for Improved Performance of Magnesium Diboride Superconductors
similarity 0.92Shi Xue Dou et al. · 2006 · arXiv:cond-mat/0602484
Source status unknown — claims are unverified
Magnetic field processing to enhance critical current densities of MgB2 superconductors
similarity 0.91S. X. Dou et al. · 2006 · arXiv:cond-mat/0601191
Source status unknown — claims are unverified