Bose-Einstein Condensation Picture of Superconductivity in High Temperature Superconductors (Dilute Metals)

Bogomolov, V. N.

Bose-Einstein Condensation Picture of Superconductivity in High Temperature Superconductors (Dilute Metals)

Bogomolov, V. N.

arXiv:cond-mat/0604509 · 2006-12-14

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Structures and parameters of some high and low temperature superconductors (HTSC, LTSC) are considered basing on the alternative estimate of the O2- ion radius magnitude (0.5-0.6) A. Phase transitions into the superconducting state are considered as the Bose-Einstein condensation (BEC). The super HTSC with Tc = 371 K (YBa2Cu3Se7) and TC ~ 400K (Ag2(Ag3Pb2H2O6)) and LTSC with Tc~0.3K (SrNbxTi(1-x)O3) are shown to be of the BEC type. Instability of the structure of the first one results from higher magnitude of the Se2- ion radius in comparison with the O2- radius. The second one forms quasi one-dimensional structures and is rather inpractical. The electron density and the effective mass are estimated for some stoichiometric and non-stoichiometric (nano-composite) high temperature superconductors, which have some peculiar features. Large effective masses can indicate existance of polarons (bipolarons) in such systems. Some new superconductors MgxWO3.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
YBa2Cu3Se7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	371	Pressure not reported	unknown
Ag2(Ag3Pb2H2O6) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	400	Pressure not reported	unknown
SrNbxTi(1-x)O3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.3	Pressure not reported	unknown
YBa2Cu3O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	90	Pressure not reported	unknown
SrTiO3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.25	Pressure not reported	unknown
SrNbxTi(1-x)O3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.28	Pressure not reported	unknown
Na0.05WO3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	90	Pressure not reported	unknown
Na0.04NH3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	180	Pressure not reported	unknown
MgxWO3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	600	Pressure not reported	unknown